Abstract:This present study mainly focuses on the influence of low-calcium circulating fluidized bed fly ash (LCFA) on the mechanical property and microstructure of cement-based materials under different curing conditions. The mechanical properties test was conducted by changing variable parameters, such as LCFA content, the internal mixing ratio of LCFA and fly ash (FA), and dry and water curing conditions. Further, the hydration products and pore structure were analyzed using XRD, FT-IR, TG-DTG, NI, SEM, and BET micro-testing technology. The strength development law of LCFA on cement-based materials is discussed. The research results show that LCFA has a certain degree of self-hardening and can be used as a cementitious material in cement-based materials. Still, the loose and porous microstructure of LCFA leads to higher water requirements, which reduces the fluidity of cement-based pastes. Water curing is favorable for promoting the development of LCFA on the long-term compressive strength of cement-based materials. When the LCFA was added to the cement, the optimal substitution ratio was 20%, and the compressive strength at 91 days reached 101 MPa. In the case of compounding LCFA and FA, when the internal mixing ratio of LCFA/FA was 3 and the total content was 20%, the mechanical properties were the highest, and the compressive strength at 91 days was 92 MPa. The microscopic analysis result shows that the cumulative hydration heat of the samples decreased significantly with the increase of dosage of LCFA. The main hydration products of cement-based materials mixed with LCFA were AFt, C-S-H gel, and Ca(OH)2. AFt and C-S-H gels are critical to the strength development of OPC-LCFA samples. The active Al2O3 and active SiO2 in LCFA were involved in hydration reactions to promote the formation of C-A-H and C-S-H gel and effectively promote the development of the mechanical properties. Overdosages of LCFA would reduce the ettringite formation rate. FA is not conducive to AFt formation in the hydration process of OPC-FA samples.

Influence of Mechanical Grinding on Pozzolanic Characteristics of Circulating Fluidized Bed Fly Ash (CFA) and Resulting Consequences on Hydration and Hardening Properties of Blended Cement

Utilization of coal gangue power generation industry by-product CFA in cement: Workability, rheological behavior and microstructure of blended cement paste

Investigating the Hydration, Mechanical Properties, and Pozzolanic Activity of Cement Paste Containing Co-Combustion Fly Ash

The Influence of Ground Fly Ash on Cement Hydration and Mechanical Property of Mortar

Effect of Additives on the Rheological and Mechanical Properties of Microfine-Cement-Based Grout

Feasibility Study of Grinding Circulating Fluidized Bed Ash as Cement Admixture

Investigation of Low-Calcium Circulating Fluidized Bed Fly Ash on the Mechanical Strength and Microstructure of Cement-Based Material

Enhancement of compressive strength of high-volume fly ash cement paste by wet grinded cement: Towards low carbon cementitious materials

How Competitive Hydration between C 3 A and C 3 S in the Fast Dissolution Stage Affects the Hydration of Low-Heat Portland Cement Blended Pastes

Investigation on Preparation and Application in Concrete of Physically Modified Fly Ash

Effect of grinding on the hydration of hydratable alumina and properties of hydratable alumina-bonded castables

The bio-activation of pozzolanic activity of circulating fluidized-bed fly ash by Paenibacilllus mucilaginosus

Study on Mechanical and Microscopic Properties of Fly Ash Cement-Based Materials in High Geothermal Environment

Influence of Particle Morphology of Ground Fly Ash on the Fluidity and Strength of Cement Paste

The Differences among the Roles of Ground Fly Ash in the Paste, Mortar and Concrete

Effect of Phosphorus Slag Admixture on the Properties and Hydration Mechanism of Circulating Fluidized Bed Fly Ash-Based Multi-Solid Waste Cementitious Material

Influence of Calcined Flue Gas Desulfurization Gypsum and Calcium Aluminate on the Strength and AFt Evolution of Fly Ash Blended Concrete under Steam Curing

Modeling of Effect of Fly Ash Amount on Microstructure and Chloride Diffusivity of Blended Fly Ash-Cement Systems

Mechanical Activation of Fly Ash from MSWI for Utilization in Cementitious Materials.

Utilization of fly ash microsphere powder as a mineral admixture of cement: Effects on early hydration and microstructure at different curing temperatures

Circulating Fluidized Bed Fly Ash Mixed Functional Cementitious Materials: Shrinkage Compensation of f-CaO, Autoclaved Hydration Characteristics and Environmental Performance