Effect of water content on microstructure and properties of magnesium potassium phosphate cement pastes with different magnesia‐to‐phosphate ratios

Jihui Qin,Jueshi Qian,Xiaobing Dai,Chao You,Hongyan Ma,Zhen Li
DOI: https://doi.org/10.1111/jace.17695
IF: 4.186
2021-02-22
Journal of the American Ceramic Society
Abstract:<p>Magnesium potassium phosphate cement (MKPC) is a class of chemically‐bonded ceramic for special engineering applications. The selection of mass ratios of MgO‐to‐KH<sub>2</sub>PO<sub>4</sub> (<i>M/P</i>) and water‐to‐cement (<i>W/C</i>) is an important aspect for formulating MKPC paste. This paper analyzed the stoichiometry of the primary reaction of MKPC and investigated the effect of <i>W/C</i> (0.14–0.40) on paste microstructure and properties at different <i>M/P</i> (1.5–4). At high <i>M/P</i>, low <i>W</i>/<i>C</i> was sufficient to complete the hydration of KH<sub>2</sub>PO<sub>4</sub> and higher <i>W/C</i> yielded looser microstructure, dictating that properties of high <i>M/P</i> pastes were monotonic functions of <i>W/C</i>. However, a clear <i>W/C</i> threshold effect was found in medium <i>M/P</i> pastes at both micro‐ and macro‐ levels. Low <i>W/C</i> below stoichiometric value suppressed the formation of K‐struvite and favored the presence of an amorphous phase, leading to intense early shrinkage, low early compressive strength and poor long‐term water resistance. The increase in <i>W/C</i> above stoichiometric value resulted in segregation of excess water and thus to porous structure, with detrimental effects on dimensional stability and strength. The micro–macro analysis highlighted the importance of stoichiometric water amount in optimal design of MKPC.</p>
materials science, ceramics
What problem does this paper attempt to address?
The paper primarily explores the performance issues of Magnesium Potassium Phosphate Cement (MKPC) under different ratios of magnesium oxide to potassium dihydrogen phosphate (M/P) and different water-to-cement ratios (W/C), particularly how these factors affect the microstructure and properties of the cement paste. The core research points of the paper include: 1. **Reaction Mechanism Analysis**: Firstly, a theoretical analysis of the main chemical reactions of MKPC was conducted to clarify the stoichiometric relationships between magnesium oxide, potassium dihydrogen phosphate, and water. Through this analysis, the optimal water-to-cement ratio required for complete reaction (W/C_min) was determined. 2. **Experimental Design**: A series of experiments were designed to study the performance of MKPC paste under different M/P and W/C conditions. The experiments considered four different M/P value groups and adjusted the corresponding W/C values. 3. **Performance Evaluation**: The performance of MKPC paste was evaluated through a series of physical tests (such as initial setting time, hydration temperature changes, etc.) and microstructural characterizations (such as X-ray diffraction, Fourier transform infrared spectroscopy, etc.). - Under high M/P conditions, a lower W/C is sufficient to complete the hydration of potassium dihydrogen phosphate, while a higher W/C leads to a more loose microstructure. - Under moderate M/P conditions, there is a significant W/C threshold effect, where too low a W/C inhibits the formation of potassium phosphate, leading to increased early shrinkage, reduced early compressive strength, and poor long-term water resistance; whereas too high a W/C results in excess water separation, forming a porous structure, which is also detrimental to dimensional stability and strength. 4. **Conclusion**: The study emphasizes the importance of stoichiometric water in the optimal design of MKPC and provides in-depth insights into the relationship between the microstructure and macroscopic properties of MKPC paste under different formulation conditions. In summary, this paper aims to address the changes in the microstructure and performance of the MKPC system under different formulation conditions, providing theoretical basis and technical guidance for the practical application of MKPC materials.