Abstract:Tungsten (W) is a potential candidate for plasma facing materials (PFMs) of fusion reactor. The helium (He) produced in fusion reaction is insoluble and easy to gather and form to He bubbles in W, resulting in embrittlement and degradation of the performance of the W matrix. In this paper, based on molecular dynamics, the nucleation and growth of helium bubbles in the bulk and at ∑3[211](110) and ∑9[110](411) grain boundaries of W was studied. As a result, the growth mechanism of Helium bubbles at grain boundary of W was different from in bulk. Helium bubbles in bulk W grow up by extruding dislocation rings. The growth mechanism of helium bubbles at ∑3[211](110) grain boundary was as follows: Firstly, a small amount of W interstitial atoms were extruded and emitted. And then the 1/2 \begin{document}$\left\langle {111} \right\rangle $\end{document} dislocation line was extruded. Finally, the 1/2 \begin{document}$\left\langle {111} \right\rangle $\end{document} dislocation line would migrate along the direction of [111] of the grain boundary interface. Moreover, the emission of W interstitial atoms and dislocation extrusion of the helium bubble were not observed in our simulated time scale at the ∑9[110](411) grain boundary. Then we used the NEB method to calculate the diffusion barrier of self-gap atoms in the bulk and at ∑3[211](110) and ∑9[110](411) grain boundaries of W, which explained the simulation results. The migration energy barrier of W self-gap atoms in the bulk and at ∑3[211](110) grain boundary was only a few to a few millielectron volts. So as long as W self-gap atoms dissociated from the surface of the He bubble in the thermal relaxation process, they can be easily migrated out. However, The migration energy of the W self-gap atom at the ∑9[110](411) grain boundary can be from a few tenths to a few electron volts. Even during the thermal relaxation process, the W self-gap atoms dissociated from the surface of the He bubble. It was difficult for the W self-gap atoms migrated out. Finally, the correlation between He bubble size and stress released was given. Either in bulk or at ∑3[211](110) and ∑9[110](411) grain boundaries of W, after the pressure of the helium bubble becomes stable with time, the radius of the helium bubble would increase rapidly whenever the pressure dropped sharply. So there was a small step on the curve of the evolution of the radius of the helium bubble with time. Thus, helium bubbles in W could promote growth by releasing pressure intermittently.

The early growth process of helium blistering in tungsten and molybdenum: First-principles and statistical model calculations

Molecular Dynamics Simulations of Helium Migration, Diffusion Behavior of Helium Bubbles, and Melting Point of Single Crystal in Bulk Γ-Fe

The nucleation and growth of Helium hubbles at grain boundaries of bcc tungsten: a molecular dynamics simulation

Effects of the Be 22 W Phase Formation on Hydrogen Retention and Blistering in Mixed Be/W Systems

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

The helium-vacancy complexes and helium bubbles formation mechanism in chromium: a comprehensive first-principle study

First-principles study of intrinsic defects and helium in tungsten trioxide

Key mechanistic features of swelling and blistering of helium-ion-irradiated tungsten

Shock response of He bubble in single crystal tungsten: molecular dynamics simulation study

Atomistic Mechanism from Vacancy Trapped H/He Atoms to Initiation of Bubble in W under Low Energy Ions Irradiation

Mechanisms of helium irradiation blistering and surface deformation in tungsten

The mobility of small vacancy/helium complexes in tungsten and its impact on retention in fusion-relevant conditions

Molecular dynamics simulations of cumulative helium bombardments on tungsten surfaces

Diffusion, Trapping, and Dissociation Behaviours of Helium at the Σ5 Grain Boundary in Tungsten: A Molecular Dynamics Study

Hydrogen Behaviors at the Near-Surface Region of Tungsten: A First-Principles Study

Modeling irradiation-induced intragranular gas bubble in tungsten under external tensile loading

First-Principles Study of Properties and Helium Behavior of Tungsten/Beryllium Interface Structure

Molecular-Dynamics Analysis of the Mechanical Behavior of Plasma-Facing Tungsten

Molecular dynamics simulation of bubble growth under surface of tungsten under helium irradiation

Growth Mechanism of Subsurface Hydrogen Cavities in Tungsten Exposed to Low-Energy High-Flux Hydrogen Plasma

Study on the Stability of Helium Clusters and Interstitials of Helium in Tungsten