Abstract:Tungsten (W) is a potential candidate for plasma facing materials (PFMs) of fusion reactor. The helium (He) produced in fusion reaction is insoluble and easy to gather and form to He bubbles in W, resulting in embrittlement and degradation of the performance of the W matrix. In this paper, based on molecular dynamics, the nucleation and growth of helium bubbles in the bulk and at ∑3[211](110) and ∑9[110](411) grain boundaries of W was studied. As a result, the growth mechanism of Helium bubbles at grain boundary of W was different from in bulk. Helium bubbles in bulk W grow up by extruding dislocation rings. The growth mechanism of helium bubbles at ∑3[211](110) grain boundary was as follows: Firstly, a small amount of W interstitial atoms were extruded and emitted. And then the 1/2 \begin{document}$\left\langle {111} \right\rangle $\end{document} dislocation line was extruded. Finally, the 1/2 \begin{document}$\left\langle {111} \right\rangle $\end{document} dislocation line would migrate along the direction of [111] of the grain boundary interface. Moreover, the emission of W interstitial atoms and dislocation extrusion of the helium bubble were not observed in our simulated time scale at the ∑9[110](411) grain boundary. Then we used the NEB method to calculate the diffusion barrier of self-gap atoms in the bulk and at ∑3[211](110) and ∑9[110](411) grain boundaries of W, which explained the simulation results. The migration energy barrier of W self-gap atoms in the bulk and at ∑3[211](110) grain boundary was only a few to a few millielectron volts. So as long as W self-gap atoms dissociated from the surface of the He bubble in the thermal relaxation process, they can be easily migrated out. However, The migration energy of the W self-gap atom at the ∑9[110](411) grain boundary can be from a few tenths to a few electron volts. Even during the thermal relaxation process, the W self-gap atoms dissociated from the surface of the He bubble. It was difficult for the W self-gap atoms migrated out. Finally, the correlation between He bubble size and stress released was given. Either in bulk or at ∑3[211](110) and ∑9[110](411) grain boundaries of W, after the pressure of the helium bubble becomes stable with time, the radius of the helium bubble would increase rapidly whenever the pressure dropped sharply. So there was a small step on the curve of the evolution of the radius of the helium bubble with time. Thus, helium bubbles in W could promote growth by releasing pressure intermittently.

Molecular dynamics simulations of cumulative helium bombardments on tungsten surfaces

Molecular dynamics simulation analysis of helium cluster growth conditions under tungsten surfaces

Crystal orientation effects on helium ion depth distributions and adatom formation processes in plasma-facing tungsten

Molecular dynamics simulation of bubble growth under surface of tungsten under helium irradiation

Simulation Study of Evolution of Helium Bubbles in Bulk Tungsten

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Hydrogen Behaviors at the Near-Surface Region of Tungsten: A First-Principles Study

Effects of temperature and surface orientation on migration behaviours of helium atoms near tungsten surfaces

Molecular dynamics simulation of helium behavior in tungsten matrix

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten

Diffusion, Trapping, and Dissociation Behaviours of Helium at the Σ5 Grain Boundary in Tungsten: A Molecular Dynamics Study

Study of interaction between low energetic hydrogen and tungsten surface by molecular dynamics simulations

Possible approaches for simulating the formation of fuzz structure on tungsten surface under helium irradiation

Cluster dynamics modeling of accumulation and diffusion of helium in neutron irradiated tungsten

Helium bubble size effects on the surface morphological response of plasma-facing tungsten

Helium segregation on surfaces of plasma-exposed tungsten

Diffusion behavior of hydrogen isotopes in tungsten revisited by molecular dynamics simulations

Revealing the synergistic effect of invisible helium clusters in helium irradiation hardening in tungsten

The nucleation and growth of Helium hubbles at grain boundaries of bcc tungsten: a molecular dynamics simulation

Mechanisms of helium irradiation blistering and surface deformation in tungsten

Microscopic Mechanism of Nucleation and Growth of Helium Bubbles in Monovacancy in Tungsten: Helium Regulates the Charged States of Tungsten Atoms