Abstract:The ductility of metallic materials is recognized to be significantly affected by stress state and strain rate. However, systematic investigations on the impacts of stress state and strain rate on ductile behavior are infrequent, and only a minority of fracture models can consider both effects concurrently. This work aims to systematically investigate the ductile response of Ti6Al4V alloy over a broad spectrum of stress states and strain rates and to propose a ductile model that incorporates the coupled influence of stress state and strain rate. First, five types of specimens were employed to obtain distinct stress states. Then, the fracture strain of material was ascertained for strain rate spanning from 10 −3 /s to 10 3 /s, stress triaxiality ranging from -0.7 to 0.4, and Lode angle parameter varying from -1 to 1 using a combined experimental-numerical method. It was found that over a broad spectrum of stress states, the relation between fracture strain versus stress state is not monotonic, and the fracture strain reduces as strain rate increases. Utilizing the experimental data, a novel ductile fracture model incorporating the stress triaxiality, Lode angle parameter and strain rate was established and embedded into the ABAQUS/Explicit through the user material subroutine VUMAT. Finally, a validation test was conducted to demonstrate the validity of the proposed model. The results indicate the satisfactory correlation between experiment and calculation for fracture displacement and fracture morphology, which illustrates that the proposed model can predict the ductile behavior across a wide spectrum of stress states and strain rates. This work provides a definite theoretical guidance for the optimization design and safety evaluation of Ti-6Al-4V alloy structural components.

Stress state dependence of ductile damage and fracture behavior: Experiments and numerical simulations

Micro-mechanical studies on the effect of the stress triaxiality and the Lode parameter on ductile damage

Numerical Analysis of Experiments on Damage and Fracture Behavior of Differently Preloaded Aluminum Alloy Specimens

Modeling of Ductile Damage and Fracture Behavior Based on Different Micromechanisms

Macroscopic damage laws based on analysis of microscopic unit cells

A ductile damage criterion at various stress triaxialities

Micromechanical Simulation of Fracture Behavior of Nanostructured Metals with Bimodal Grain Size Distribution

Damage and fracture initiation under shear and compression stress states in the aluminum alloy EN AW6082-T6

Experimental techniques for ductile damage characterisation

Experiments on Low–Cycle Ductile Damage and Failure Under Biaxial Loading Conditions

Stress-state dependency of ductile fracture in an extruded magnesium alloy and its underlying mechanisms

Ductile damage evolution under triaxial state of stress: theory and experiments

Coupled effect of stress state and strain rate on ductile fracture of Ti6Al4V alloy

Experimental analysis of strain path dependent ductile damage mechanics and forming limits

Experimental and Numerical Investigation of Ductile Fracture of Carbon Steel Structural Components

Biaxial Experiments and Numerical Analysis on Stress-State-Dependent Damage and Failure Behavior of the Anisotropic Aluminum Alloy EN AW-2017A

Continuum damage mechanics modelling incorporating stress triaxiality effect on ductile damage initiation

Effect of stress triaxiality and normalized Lode angle on ductile fracture of aluminum 2139-T8

Analysis of ductile damage and fracture under reverse loading

Dependence of ductile fracture on stress triaxiality factor

A phase field model for ductile fracture considering the strain rate, stress triaxiality and Lode angle parameter