Programmable, UV-Printable Dielectric Elastomers Actuate at Low Voltage without Prestretch and Supporting Frames

Ramadan Borayek,Pengpeng Zhang,Habimana J. Willy,Mostafa Zedan,Jian Zhu,Jun Ding

DOI: https://doi.org/10.1021/acsaelm.0c00837

IF: 4.494

2020-12-04

ACS Applied Electronic Materials

Abstract:Dielectric elastomers are soft and perfect insulator polymers able to produce large strains with high energy density under the effect of applied high voltage. However, their use in practical applications is hindered by the need for high voltage to actuate. Also, they need prestretching between rigid frames to produce out-of-plane shape changes, which may reduce their lifetime. Here, we synthesized a set of elastomers with high permittivity (from 20 to reach 60 at 10³ Hz), controllable thermal properties (<i>T</i>_g vary from −15 to −50 °C), and good mechanical properties (Young's modulus values between 0.48 and 0.2 MPa at 20% strain). Due to the high permittivity, an actuator made of the material was able to respond to a low voltage of 700 V and produce a 6.5% area strain for more than 10 000 cycles. Moreover, the elastomers were found to produce giant free-end bending displacements with prespecified bending direction (bend to the side of the positive electrode) under a low electric field, which we called programmable dielectric elastomers (PDE). Besides the aforementioned characteristics and performance, the formulated elastomers are suitable for UV-based three-dimensional (3D) printing. The printability of the elastomers allows fabricating programmable complex geometries to produce high deformations under relatively low electric fields.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaelm.0c00837?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaelm.0c00837</a>.Printing parameters for successfully printed parts from different elastomer formulations of 100 μm layer thickness using an Asiga printer (Table S1); chemical formulation and summary of mechanical properties (Table S2); FTIR results (Figure S1); Curing depth versus exposure time for different light stabilizers amounts and curing depth versus exposure time for different amounts of photoinitiator (Figure S2); FTIR results (Figure S3); TGA results, DSC results, and gel extraction efficiency results (Figure S4); electrochemical results (Figure S5); response of the investigated elastomers during and after charging cycle (Figure S6); Set of 30 samples printed one patch for testing the bending direction and simple test rig to randomly test the printed samples (Figure S7); Yeoh's model fitting of experimental data (Figure S8); model and assumptions proposed for modeling electromechanical behavior of the elastomers and distribution of Maxwell's stresses in the actuated area (Figure S9); and simulations results showing the dependence of <i>Z</i> bending displacement on applied voltage (Figure S10) (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00837/suppl_file/el0c00837_si_001.pdf">PDF</a>)Elastic stretchability of printed piece of elastomer and elastic cyclic compression of a complex lattice (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00837/suppl_file/el0c00837_si_002.mp4">MP4</a>)Breakdown strength phenomenon of elastomer (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00837/suppl_file/el0c00837_si_003.mp4">MP4</a>)Demonstration of the actuation performance of elastomer (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00837/suppl_file/el0c00837_si_004.mp4">MP4</a>)Proof-of-concept applications for soft gripper application (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00837/suppl_file/el0c00837_si_005.mp4">MP4</a>)Stability of membrane for 10 000 s under 700 V at 0.5 Hz (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00837/suppl_file/el0c00837_si_006.mp4">MP4</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,engineering, electrical & electronic