Effects of alkali activator on the chloride-ion permeability of one-part alkali-activated nickel slag concrete

Xuefang Wang,Qiaoling Lan,Huanghua Lin,Yasi Wang,Wenda Wu,Liwei Xu,Lifang Fu,Chunhui Li

DOI: https://doi.org/10.1016/j.cscm.2024.e02970

IF: 4.934

2024-02-18

Case Studies in Construction Materials

Abstract:Herein, the effects of the ionic types and content of alkali activator on the chloride-ion permeability of one-part alkali-activated nickel slag concrete were examined. The NT Build 492 method was adopted to measure the Cl − transport performance. In general, the total Cl − concentration in concrete decreases with the increase of penetration depth; however, the enrichment of Cl − concentration in the sample is not obvious. Anions have more effect on 28-d compressive strength, while cations have more effect on chlorine-ion permeability. For the same Na 2 O content, SiO 3 2− -activator and Na + -activator perform better than other anions and cations, while OH – and K + perform worse than other ions. The chloride-ion permeability coefficient ( D RCM ) of concrete with Na 2 SiO 3 is the lowest and that with KOH is the highest. The D RCM of concrete prepared with KOH is 1.93 times higher than that of concrete prepared with Na 2 SiO 3 . When the activator is Na 2 SiO 3 , the D RCM of concrete decreases with the increase in Na 2 O content when the Na 2 O content is less than 7%. However, when the Na 2 O content exceeds 7%, the D RCM of concrete increases with the increase in Na 2 O content.

construction & building technology,materials science, multidisciplinary,engineering, civil