Abstract:Purpose Fused deposition modeling (FDM) nowadays offers promising future applications for fabricating not only thermoplastic-based polymers but also composite PLA/Metal alloy materials, this capability bridges the need for metallic components in complex manufacturing processes. The research is to explore the manufacturability of multi-metal parts by printing green bodies of PLA/multi-metal objects, carrying these objects to the debinding process and varying the sintering parameters. Design/methodology/approach Three different sample types of SS316L part, Inconel 718 part and bimetallic composite of SS316L/IN718 were effectively printed. After the debinding process, the printed parts (green bodies), were isothermally sintered in non-vacuum chamber to investigate the fusion behavior at four different temperatures in the range of 1270 °C−1530 °C for 12 h and slowly cooled in the furnace. All samples was assessed including geometrical assessment to measure the shrinkage, characterization (XRD) to identify the crystallinity of the compound and microstructural evolution (Optical microscopy and SEM) to explore the porosity and morphology on the surface. The hardness of each sample types was measured and compared. The sintering parameter was optimized according to the microstructural evaluation on the interface of SS316L/IN718 composite. Findings The investigation indicated that the de-binding of all the samples was effectively succeeded through less weight until 16% when the PLA of green bodies was successfully evaporated. The morphology result shows evidence of an effective sintering process to have the grain boundaries in all samples, while multi-metal parts clearly displayed the interface. Furthermore, the result of XRD shows the tendency of lower crystallinity in SS316L parts, whilst IN718 has a high crystallinity. The optimal sintering temperature for SS316L/IN718 parts is 1500 °C. The hardness test concludes that the higher sintering temperature gives a higher hardness result. Originality/value This study highlights the successful sintering of a bimetallic stainless steel 316 L/Inconel 718 composite, fabricated via dual-nozzle fused deposition modeling, in a non-vacuum environment at 1500 °C. The resulting material displayed maximum hardness values of 872 HV for SS316L and 755.5 HV for IN718, with both materials exhibiting excellent fusion without any cracks.

Study on the Forming and Mechanical Properties of 17-4PH Parts Fabricated by Metal Material Extrusion Additive Manufacturing Technique

Mechanical and Thermal Analyses of Metal-PLA Components Fabricated by Metal Material Extrusion

Creating Metal Parts by Fused Deposition Modeling and Sintering

The enhancement of mechanical properties via post-heat treatments of AISI 630 parts printed with material extrusion

Mechanical, Electrical, and Thermal Characterization of Pure Copper Parts Manufactured via Material Extrusion Additive Manufacturing

Study on Performance of Metal and Polymer Composites Parts Based by Additive Manufacturing

Mechanical Properties and Fatigue Performance of 17-4 PH Stainless Steel Manufactured by Atomic Diffusion Additive Manufacturing Technology

Material extrusion additive manufacturing of 17–4 PH stainless steel: effect of process parameters on mechanical properties

17-4 PH Steel Parts Obtained through MEX and PBF-LB/M Technologies: Comparison of the Structural Properties

Mesostructured emerging 316L-17-4PH composite steel parts by material extrusion for the property maximization through an efficient microstructural design

Microstructural, Mechanical, and Electrochemical Corrosion Properties of Extrusion Additive Manufactured 17-4 Precipitation Hardenable Stainless Steel

Strength Properties of 316L and 17-4 PH Stainless Steel Produced with Additive Manufacturing

Material extrusion-based fabrication of 316L stainless steel: analysis of debinding and sintering, mechanical properties, and corrosion resistance

Microstructure and Defect Analysis of 17-4PH Stainless Steel Fabricated by the Bound Metal Deposition Additive Manufacturing Technology

Printing, Debinding and Sintering of 15-5PH Stainless Steel Components by Fused Deposition Modeling Additive Manufacturing

Sintering parameter investigation for bimetallic stainless steel 316L/inconel 718 composite printed by dual-nozzle fused deposition modeling

Microstructure evolution, phase formation, corrosion, and mechanical properties of stainless steel fabricated by extrusion-based sintering-assisted additive manufacturing

Influence of Sintering Process Parameters on Properties and Dimensional Accuracy of MIM17-4PH Stainless Steel

Anisotropic sintering shrinkage behavior of stainless steel fabricated by extrusion-based metal additive manufacturing

Direct Metal Part Forming of 316L Stainless Steel Powder by Electron Beam Selective Melting

Experimental Investigation on Selective Laser Melting of 17-4PH Stainless Steel