Influence of Particle Size of Lignite‐Based Hard Carbon on Sodium Storage Performance
Zhitao Yang,Yukuan Wei,Gang Liu,Leilei Zhang,Tengfei Huang,Haohao Xue,Yuhang Zhang,Zishun Lin
DOI: https://doi.org/10.1002/slct.202404647
2024-12-05
ChemistrySelect
Abstract:Lignite‐based hard carbon was utilized as the anode material for sodium‐ion batteries (SIBs), and the influence of hard carbon particle size on its electrochemical performance was investigated. The results show that smaller particle sizes in the hard carbon anode lead to a reduction in mesopore volume, specific surface area, and coating density, which in turn significantly enhance the cycle stability, initial coulombic efficiency (ICE), and rate capability of the electrode. The particle size of hard carbon used as an anode material for sodium‐ion batteries (SIBs) directly affects critical physical properties, including specific surface area and conductivity of the electrode, thereby influencing the electrode's sodium storage performance. However, related research is limited. In this work, lignite‐derived hard carbons with various particle sizes were investigated as anode materials for SIBs. The electrochemical performance and Na+ diffusion capability were evaluated. The results show that smaller particle sizes in hard carbon anodes lead to reduced mesopore volumes, specific surface areas, and coating densities, which effectively improve cycle stability, initial coulombic efficiency (ICE), and rate capability of the electrode. Specifically, hard carbon anodes within a 1–15 μm particle size distribution exhibited a reversible capacity of 251 mAh g−1 and an ICE of 73.67% at a current density of 25 mA g−1. Even after 100 cycles at 0.2 C, these anodes maintained a reversible capacity of 238 mAh g−1, achieving a capacity retention rate of 99.85%.
chemistry, multidisciplinary