Shihao Zhou,Yuanchang Lai,Junchi Ma,Bin Liu,Nannan Ni,Feng Dai,Yahong Xu,Zhaodi Wang,Xin Yang
Abstract:Structural damping composites exhibit considerable potential in aerospace and other fields due to their excellent damping and vibration reduction performance, as well as their structural carrying capacity. However, conventional structural damping composite materials generally do not combine excellent mechanical and damping properties at the same time, which makes it difficult for them to meet the practical demand in engineering. In this paper, polyetherimide (PEI) non-woven fabric interlayer materials loaded with quantified polydopamine (PDA) and carboxylated multi-walled carbon nanotubes (MWCNTs-COOH) were used to prepare carbon fiber-reinforced bismaleimide composites through the co-curing process. The mechanical and damping properties of the composites were systematically studied. The results demonstrate that PEI non-woven fabric interlayers loaded with PDA and MWCNTs-COOH can synchronously improve the mechanical and damping properties of the co-cured composites. The incorporation of carbon nanotubes and polydopamine during the co-curing process synergistically improves the flexural strength, flexural modulus, interlaminar shear strength, and impact fracture toughness of the composites. Most importantly, damping properties show an increase of 45.0% in the loss factor of the co-cured composites. Moreover, the reinforcement mechanism was investigated using the optical microscopy and scanning electron microscopy, which indicated that the PEI interlayers loaded with carbon nanotubes and polydopamine form a rich resin area between the layers of the composites.
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve
The paper aims to address the issue of balancing mechanical performance and damping performance in traditional structural damping composite materials. Specifically, traditional structural damping composites often cannot simultaneously possess excellent mechanical properties (such as flexural strength, modulus, interlaminar shear strength, and impact fracture toughness) and damping performance (such as loss factor), making it difficult for them to meet engineering practical needs.
### Background and Motivation
With the increase in the maneuverability and flight speed of aerospace vehicles, the demand for vibration control is also increasing. Traditional viscoelastic damping materials have issues such as low mechanical strength, aging failure, and delamination, which cannot meet these requirements. Therefore, co-cured composites that combine structural load-bearing capacity and damping vibration reduction capability have become the main trend in the development of composites. However, commonly used co-curing additives (such as viscoelastic rubber) often lead to a sharp decline in the elastic modulus and heat resistance of the composites due to their low glass transition temperature. Additionally, using high-damping viscoelastic materials as interlayer materials for composites generally results in a mechanical performance decrease of more than 40%. Therefore, new interlayer materials and damping energy dissipation mechanisms need to be developed to prepare co-cured composites.
### Solution
To simultaneously improve the mechanical and damping performance of composites, the authors used polyetherimide (PEI) nonwoven fabric as the interlayer material, loaded with a quantitative amount of polydopamine (PDA) and carboxylated multi-walled carbon nanotubes (MWCNTs-COOH). Through the co-curing process, carbon fiber-reinforced bismaleimide composites were prepared. The research results show that the PEI nonwoven fabric interlayer material loaded with PDA and MWCNTs-COOH can simultaneously improve the mechanical and damping performance of the co-cured composites. Specifically, the flexural strength, flexural modulus, interlaminar shear strength, and impact fracture toughness of the composites were significantly enhanced, and the loss factor increased by 45.0%.
### Experimental Methods
1. **Material Preparation**: PEI nonwoven fabric, carboxylated multi-walled carbon nanotubes, dopamine hydrochloride, etc.
2. **Preparation of MWCNTs/PEI Interlayer Material**: Prepared by solution impregnation method.
3. **Preparation of MWCNTs@PDA/PEI Interlayer Material**: The MWCNTs/PEI interlayer material was soaked in a dopamine monomer solution to polymerize dopamine on the surface of MWCNTs/PEI.
4. **Preparation of Three Types of Structural Damping Composites**: PEI nonwoven fabric, MWCNTs/PEI interlayer material, and MWCNTs@PDA/PEI interlayer material were respectively inserted and composites were prepared through the co-curing process.
5. **Characterization and Testing**: Including chemical composition analysis (XPS, FTIR), static mechanical performance testing (flexural performance, interlaminar shear strength, impact performance), dynamic mechanical performance testing (DMA), etc.
### Results and Discussion
1. **Static Mechanical Performance**: The flexural strength, flexural modulus, and interlaminar shear strength of MWCNTs@PDA/PEI composites increased by 9.50%, 14.96%, and 7.08%, respectively, showing the best mechanical performance.
2. **Dynamic Mechanical Performance**: The storage modulus of MWCNTs@PDA/PEI composites was the highest, and the loss factor significantly increased, indicating excellent damping performance.
### Conclusion
By loading PDA and MWCNTs-COOH into the PEI nonwoven fabric interlayer material, the mechanical and damping performance of co-cured composites can be effectively improved, making them have broad application prospects in fields such as aerospace.