Abstract:This study examined the development of Fe2B (diiron boronize) coatings on the surface of 35NiCrMo4 steel through the thermochemical surface hardening process called boronizing. The morphology and thickness of the boronize coatings were assessed using Scanning Electron Microscopy (SEM) and optical microscopy (OM). A novel mathematical mass transfer model was developed to estimate the diffusion coefficients of boron in hard coating. The presence of uniformly distributed boronize coatings with a typical sawtooth pattern on the surface of the substrate was confirmed. The boronize coating's chemical composition and phase constituents were analyzed utilizing X-ray energy dispersive spectroscopy (EDS) and X-ray diffraction analysis (XRD). The study confirmed the presence of a single-phase boronize coating (Fe2B). Furthermore, microhardness tests indicated that the boronized specimen's surface demonstrated an average hardness of approximately 1953 HV. The wear study were conducted using the pin-on-disk method under dry debonding conditions at room temperature to estimate the coefficient of friction (COF) of the boronized (average ≈ 0.35) and untreated (0.725) specimens. The results revealed approximately 200% improvement in wear resistance due to the boronized coating. The empirical validation of the mathematical model was carried out for two additional boronizing conditions at 1223 K for 3 h and 1273 K for 1.5 h, resulting in an estimated percentage error of around 2.5% for both conditions. Additionally, an ANOVA analysis was performed, taking into account the temperature and time factors. The findings indicate that both factors exert a substantial influence on the dependent variable (u), with temperature (T) contributing 64.68%, time (t) contributing 27.37%, and the interaction of both factors (T × t) contributing 5.13%.

Corrosion Behaviour of Boronized Ductile irons in Formic and Nitric Acid Solutions

Effect of Boronizing on the Corrosion Resistance of Martensitic Stainless Steels

Corrosion-abrasion wear resistance of 28%Cr white cast iron containing boron

Investigations of Microstructures and Erosion–Corrosion Performance of Cast Boron-Bearing Stainless Steel

CORROSION BEHAVIOR OF 304,254 SMO AND Hastelloy C-276 IN HAc SOLUTION CONTAINING Br~- ION

Effect of Boronising on Mechanical Properties, Wear and Corrosion of N80 Steel

Comparative Erosion–corrosion and Electrochemical Studies of Ni Austenitic Cast Iron in Acidic Slurry Medium

Investigation of Tribological Behavior of Coated and Untreated Rail Steels Under Wet Conditions

Effect of Silicon and Graphite Degeneration on High-Temperature Oxidation of Ductile Cast Irons in Open Air

Effect of Temperature and Concentration on the Corrosion Behavior of 42CrMoE Low Alloy Steel in Boric Acid Solution

The Effect of Boron Addition on the corrosion behavior of Ni Cr Modental alloy prepared by powder metallurgy.

Influence of Boron Concentration on the Corrosion Resistance of High Boron White Cast Iron to Liquid Zinc Bath

Effect of Boron Content in LiOH Solutions on the Corrosion Behavior of Zr-Sn-Nb Alloy

Corrosion Behaviour of 316L Stainless Steel in Boric Acid Solutions

Corrosion Behavior of Stainless Steels and Nickel-Based Alloys in Acetic Acid Solutions Containing Bromide Ions

Corrosion potential and theoretical studies of fabricated Schiff base for carbidic austempered ductile iron in 1M H2SO4 solution

Corrosion Resistance of Austenitic NiMn-Nodular Cast Iron in NaCl Solution

Examination of Wear and Rockwell-C adhesion Properties of Nitronic 50 Steel Coated with Pack Boriding Method

Boronize Coatings Studied with a New Mass Transfer Model

Investigating the erosive wear characteristics of AISI 420 martensitic stainless steel after surface hardening by boriding

Influence of Boron on Microstructure and Mechani cal Properties of Abrasive Wear Resistant Ductile Cast Iron