Ultra-stable Pd ions at Al T1/T2 sites on a dealuminated Pd/beta passive NO x adsorber

Yi Zhu,Jun Wang,Chen Wang,Jianqiang Wang,Gurong Shen,Meiqing Shen

DOI: https://doi.org/10.1039/d3cy00430a

2023-05-18

Abstract:Pd ions as NO adsorbing sites on zeolites for PNA materials showed evident deactivation when exposed to reducing agents or treated under hydrothermal conditions. In this study, stable Pd 2+ species are mainly obtained by loading palladium on a dealuminated beta zeolite, and can survive during cyclic evaluations with reducing agents and hydrothermal treatment at 850 °C. On the dealuminated beta zeolite, a large amount of framework Al T1/T2 is reserved by design. CO-DRIFTS and H 2 -TPR results reveal that [Pd–OH] and isolated Pd(iso) b are mainly present on the dealuminated beta zeolite and are quite stable because of their higher energy. These [Pd–OH]/Pd(iso) b on the dealuminated beta zeolite contribute stable NO x storage performance. 27 Al MAS NMR suggests that the Al T1/T2 sites of PDB-F are more stable and the [Pd–OH]/Pd(iso) b simultaneously protects the occupied Al T1/T2 sites from being destroyed. NH 3 -TPD shows that [Pd–OH]/Pd(iso) b on the dealuminated beta zeolite contributes a more stable acid concentration after cycle evaluation or hydrothermal aging. Thus, the dealuminated Pd/beta materials, with ultra-stable Pd 2+ species, can meet real exhaust conditions.

chemistry, physical