Abstract:Zeolites with different framework structures (SSZ-13, ZSM-5, BEA) but similar Si/Al ratios (~ 12–15) and Pd loading (~ 1 wt%) were synthesized and evaluated as low-temperature passive NOx adsorbers (PNA). These materials exhibit high NOx adsorption efficiency with atomically dispersed Pd being the active adsorption site. Hydrothermal aging at 750 °C for 16 h in the presence of 10% water vapor in air resulted in the formation of PdO nanoparticles in all three samples as evidenced by high-energy XRD. Hydrothermal aging of the small-pore 1–3 wt% Pd/SSZ-13 (Si/Al = 6) materials, which contain ~ 100–90% atomically dispersed palladium ions, decreases its PNA performance only by ~ 10–20%, indicating agglomeration of only ~ 10–20% of atomically dispersed Pd into PdO. High-field solid state 27Al NMR studies on the fresh and aged samples reveal dealumination and significant changes in the distribution of Al (and thus, Brönsted acid) sites after hydrothermal aging. FTIR measurements with NO probe molecule and titration of Brönsted acid sites with nitrosyl (NO+) ions further corroborate the 27Al NMR data. Because framework aluminum atoms are the anchoring sites for atomically dispersed Pd ions, their elution from the framework causes the loss of active atomically dispersed Pd species. With the aid of HAADF-STEM imaging and synchrotron XRD studies, we further confirm and visualize the fate of these Pd species: they agglomerate into PdO nanoparticles on the external surface of zeolite. Consequently, these changes lead to the decrease in PNA performance of these materials after hydrothermal aging. The thus formed PdO agglomerates cannot be re-dispersed back to their ionic state due to the loss of framework Al T-sites and/or inherent stability of such large PdO particles. Our study demonstrates that, unlike in previous studies that found increased PNA performance upon HTA, high temperatures hydrothermal aging of PNA materials that contain atomically dispersed Pd initially results in a decrease in NOx storage efficiency due to the formation of PdO agglomerates. However, we also highlight the high hydrothermal stability of predominantly atomically dispersed 1–3 wt% Pd/SSZ-13 (Si/Al = 6), whose performance decreases only marginally after prolonged hydrothermal aging at 750 °C. This study shows that hydrothermally stable passive NOx materials can be prepared using small-pore SSZ-13 zeolite.

Superior performance in passive NOx adsorption over an Al-rich Beta zeolite supported palladium

Ultra-stable Pd ions at Al T1/T2 sites on a dealuminated Pd/beta passive NO x adsorber

Effects of Si/Al Ratio on Passive NOx Adsorption Performance over Pd/Beta Zeolites

The upgrading role of Al at T1/T2 sites in stabilizing Pd ions over Pd-beta passive NOx adsorbers under a reducing atmosphere

Enhancing the NOx storage and hydrothermal stability of Pd/SSZ-13 passive NOx adsorbers by regulating the Al distributions

The Influence of Si/Al Ratios on Adsorption and Desorption Characterizations of Pd/Beta Served As Cold-Start Catalysts

Cold-Start NOx Mitigation by Passive Adsorption Using Pd-Exchanged Zeolites: From Material Design to Mechanism Understanding and System Integration

Palladium-assisted NOx Storage and Release on CexZr1-xO2 for Passive NOx Adsorber in Diesel Exhaust Aftertreatment

Effects of alkali and alkaline earth metals on the activity and stability of Pd/SSZ-13 for passive NO x adsorption

Unexpected Low Temperature Activity with Low N2 O Emission of Stabilized Al-rich Zeolite Beta for Selective Catalytic Reduction of NOx

The upgrading role of Al at T1/T2 sites in stabilizing Pd ions over Pd-beta passive NO x adsorbers under a reducing atmosphere

Recent progress of Pd/zeolite as passive NOx adsorber: Adsorption chemistry, structure-performance relationships, challenges and prospects

Palladium/Zeolite Low Temperature Passive NOx Adsorbers (PNA): Structure-Adsorption Property Relationships for Hydrothermally Aged PNA Materials

Optimizing the Proportion of Framework Elements and the Distribution of Active Sites in Pd–SSZ-13 for Better Passive NOx Adsorber Performance

Low Temperature NO Storage of Zeolite Supported Pd for Low Temperature Diesel Engine Emission Control

Ultrafine Pt Particles Directed by Polyvinylpyrrolidone on Zeolite Beta As an Efficient Low-Temperature H2-SCR Catalyst

A High Effective Adsorbent of NOx: Preparation, Characterization and Performance of Ca-beta Zeolites

Correlation between zeolitic particle size and the low-temperature NOx storage capacity of Pd/ZSM-11 passive NOx adsorber

The Superior Hydrothermal Stability of Pd/SSZ-39 in Low Temperature Passive NOx Adsorption (PNA) and Methane Combustion

Discovering the Remarkable Denox Activity and Anti-K Poisoning of MnFeOx/H-Beta Composite Catalyst

A Novel Material for Passive NOx Adsorber: Ce-based BEA Zeolite