Abstract:Zeolites with different framework structures (SSZ-13, ZSM-5, BEA) but similar Si/Al ratios (~ 12–15) and Pd loading (~ 1 wt%) were synthesized and evaluated as low-temperature passive NOx adsorbers (PNA). These materials exhibit high NOx adsorption efficiency with atomically dispersed Pd being the active adsorption site. Hydrothermal aging at 750 °C for 16 h in the presence of 10% water vapor in air resulted in the formation of PdO nanoparticles in all three samples as evidenced by high-energy XRD. Hydrothermal aging of the small-pore 1–3 wt% Pd/SSZ-13 (Si/Al = 6) materials, which contain ~ 100–90% atomically dispersed palladium ions, decreases its PNA performance only by ~ 10–20%, indicating agglomeration of only ~ 10–20% of atomically dispersed Pd into PdO. High-field solid state 27Al NMR studies on the fresh and aged samples reveal dealumination and significant changes in the distribution of Al (and thus, Brönsted acid) sites after hydrothermal aging. FTIR measurements with NO probe molecule and titration of Brönsted acid sites with nitrosyl (NO+) ions further corroborate the 27Al NMR data. Because framework aluminum atoms are the anchoring sites for atomically dispersed Pd ions, their elution from the framework causes the loss of active atomically dispersed Pd species. With the aid of HAADF-STEM imaging and synchrotron XRD studies, we further confirm and visualize the fate of these Pd species: they agglomerate into PdO nanoparticles on the external surface of zeolite. Consequently, these changes lead to the decrease in PNA performance of these materials after hydrothermal aging. The thus formed PdO agglomerates cannot be re-dispersed back to their ionic state due to the loss of framework Al T-sites and/or inherent stability of such large PdO particles. Our study demonstrates that, unlike in previous studies that found increased PNA performance upon HTA, high temperatures hydrothermal aging of PNA materials that contain atomically dispersed Pd initially results in a decrease in NOx storage efficiency due to the formation of PdO agglomerates. However, we also highlight the high hydrothermal stability of predominantly atomically dispersed 1–3 wt% Pd/SSZ-13 (Si/Al = 6), whose performance decreases only marginally after prolonged hydrothermal aging at 750 °C. This study shows that hydrothermally stable passive NOx materials can be prepared using small-pore SSZ-13 zeolite.

Enhancing the NOx storage and hydrothermal stability of Pd/SSZ-13 passive NOx adsorbers by regulating the Al distributions

The Superior Hydrothermal Stability of Pd/SSZ-39 in Low Temperature Passive NOx Adsorption (PNA) and Methane Combustion

The influence of phosphorus and CO poisoning on Pd/SSZ-13 with different Al distributions as passive NOx adsorbers

Effects of alkali and alkaline earth metals on the activity and stability of Pd/SSZ-13 for passive NO x adsorption

Na Cocations and Hydrothermal Aging Cooperatively Boost the Regeneration of Phosphorus-Poisoned Pd/SSZ-13 for Passive NO x Adsorption

Palladium/Zeolite Low Temperature Passive NOx Adsorbers (PNA): Structure-Adsorption Property Relationships for Hydrothermally Aged PNA Materials

Ultra-stable Pd ions at Al T1/T2 sites on a dealuminated Pd/beta passive NO x adsorber

Superior performance in passive NOx adsorption over an Al-rich Beta zeolite supported palladium

Deactivation of Pd/SSZ-13 by Potassium and Water for Passive NOx Adsorption

Investigation of crystal size effect on the NOx storage performance of Pd/SSZ-13 passive NOx adsorbers

Atomic layer deposition of silica to improve the high-temperature hydrothermal stability of Cu-SSZ-13 for NH3 SCR of NOx

The upgrading role of Al at T1/T2 sites in stabilizing Pd ions over Pd-beta passive NOx adsorbers under a reducing atmosphere

Elucidating the Key Active Sites and Impact of Silanol Defects over Pd/Ssz-13 As Pna Catalyst

Effects of Si/Al Ratio on Passive NOx Adsorption Performance over Pd/Beta Zeolites

Effects of Zr Addition on the Performance of the Pd-Pt/Al 2 O 3 Catalyst for Lean-Burn Natural Gas Vehicle Exhaust Purification

Palladium-assisted NOx Storage and Release on CexZr1-xO2 for Passive NOx Adsorber in Diesel Exhaust Aftertreatment

Enhanced hydrothermal stability of Cu-SSZ-13 by compositing with Cu-SAPO-34 in selective catalytic reduction of nitrogen oxides with ammonia

Hydrothermally Stable ZnAl2O4 Nanocrystals with Controlled Surface Structures for the Design of Long-Lasting and Highly Active/selective PdZn Catalysts

Revealing the mechanism of K-enhanced Cu-SSZ-13 catalysts against hydrothermal aging and P-poisoning for NOx reduction by NH3-SCR

Recent progress of Pd/zeolite as passive NOx adsorber: Adsorption chemistry, structure-performance relationships, challenges and prospects

A Study of CeSnO x and Pd/CeSnO x as Low-Temperature NO x Adsorbers with Excellent Hydrothermal Stability