Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

In-situ multiscale shear failure of a bistable composite tape-spring

Progressive failure analysis of 2D woven composites at the meso-micro scale

Experimental and Numerical Investigation on Shear Failure Behavior of Rock-like Samples Containing Multiple Non-Persistent Joints

Adiabatic Shear Fractures and Fragments of Cylindrical Structures under Internal Explosive Loading

Development of Multi-Scale Computation Framework to Investigate the Failure Behavior of the Materials

Bending Deformable Tension-Shear Model for Nacre-Like Composites

On tailoring deployable mechanism of a bistable composite tape-spring structure

Multiscale Analysis of Fracture of Carbon Nanotubes Embedded in Composites

Morphology characterization and in-situ three-dimensional strain field monitor of short carbon fiber-reinforced polymer composites under tension

Folding mechanics of a bistable composite tape-spring for flexible mechanical hinge

Biaxial tensile failure of short carbon-fibre-reinforced PEEK composites

Smart driving of a bilayered composite tape-spring structure

Experimental investigation and multiscale simulation on the bending fatigue of SiCf/SiC composite vanes

Multiscale Numerical Scheme on Shear Failure Feature of 3dowc/cs Bar Incorporating Microlevel Uncertainties and Coupled Constitutive Behavior

Shear behavior and failure analysis of a composite T-joint with a cutout

Mechanics of Pure Bending and Eccentric Buckling in High-Strain Composite Structures

An Adaptive Stochastic Multi-Scale Method for Cohesive Fracture Modelling of Quasi-Brittle Heterogeneous Materials under Uniaxial Tension

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Multiscale analysis method and experiments for the fracture toughness optimization analysis of carbon nanotube-epoxy composites

Frictional Sliding of Microcracks under Compression

Atomistic Simulations of the Nonlinear Deformation and Damage Modes of Super Carbon Nanotubes