Abstract:Carbon-fiber reinforced composites are made up of three different phases. Tensile or compressive deformation in the longitudinal (fiber) orientation is controlled by the fibers, leading to a linear stress strain response which ends abruptly when the fibers fail by tensile fracture or kinking in compression. Conversely, major non-linear deformations can develop under transverse compression or in-plane shear because deformation is controlled by the polymeric matrix and the interphase.In this paper, first the V-notched rail shear test was used to research the mechanical properties of composite under in-plane shear loading, and the fracture surfaces of failed specimens were examined using scanning electron microscopy (SEM). The broken samples showed a large residual shear displacement. For [0/90](8s) cross-ply laminate V-notched beam test, the failure mode is the interactions of intralaminar and interlaminar failure. The intralaminar interfacial debonding, matrix cracking and interlaminar degradation occurs in succession. Then a representative volume element (RVE) of fiber random distribution was established, with two dominant damage mechanisms-matrix plastic deformation and interfacial debonding included in the simulation by the extended Drucker-Prager model and cohesive zone model respectively. The simulation results clearly reveal the damage process of the composites and the interactions of different damage mechanisms. It can be concluded that the in-plane shear fracture initiates as interfacial debonding and evolves as a result of interactions between interfacial debonding and matrix plastic deformation. The progressive damage process and final failure mode of in-plane shear model which are based on constitute are very consistent with the observed result under SEM of V-notched rail shear test. Also a transverse shear model was established as contrast in order to comprehensively understand the mechanical properties of composite materials under shear loading, and the progressive damage process and final failure mode of composite under transverse shear loading were researched.

Shear behavior and failure analysis of a composite T-joint with a cutout

Failure Mechanism and Strength Prediction Model of T-Joint of Composite Sandwich Structure

Investigations on the Mechanical Properties of Composite T-Joints with Defects under Bending Loading

Investigating the Effects of Contact Area and Chamfering on the Failure Behavior of Plain Woven Composite-Metal T-joints

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Tensile Failure Analysis of Carbon Fiber Composite Material L-shaped Joint

Experimental and Numerical Study on Failure Behaviors of Composite Grid Stiffeners under Tensile and Flexural Loading

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

Microscopic Progressive Damage And Failure Analysis Of Carbon-Fiber Reinforced Composite Under Shear Loading

Investigation of the out-of-plane load-bearing capacity of T1100/5405 composite T-stiffened panels

Numerical and Experimental Analysis of Delamination in the T-Stiffener Integrated Composite Structure

Strength prediction of composite π joint under bending load and study of geometric and material variations effects

STRENGTH ANALYSIS OF FIBER REINFORCED COMPOSITE LAMINATES WITH BIG CUTOUTS 1)

Three-dimensional progressive damage models for cohesively bonded composite π joint

Investigation on the Progressive Damage and Bearing Failure Behavior of Composite Laminated Bolted Joints under Tension

Experimental and Multiscale Numerical Investigation on Failure Behavior of Satin Woven Carbon/carbon Composites Subjected to Pin-Loading

Experimental and Finite Element Research on the Failure Mechanism of C/C Composite Joint Structures under Out-of-Plane Loading

Influence of Failure-Load Prediction in Composite Single-Lap Joints with Brittle and Ductile Adhesives Using Different Progressive-Damage Techniques

Initial Damage Induced by Thermal Residual Stress and Microscopic Failure Analysis of Carbon-Fiber Reinforced Composite under Shear Loading

Failure prediction of marine non-planar composite π joints based on combined 2D material model and progressive damage method

Shear Mechanism of a Novel SFCBs-Reinforced Composite Shear Connector: Experimental, Theoretical Investigations and Numerical Model