Mechanical Properties of Polymers Recovered from Multilayer Food Packaging by Nitric Acid

Agnė Šleiniūtė,Tamari Mumladze,Gintaras Denafas,Vidas Makarevičius,Rita Kriūkienė,Maksim Antonov,Saulius Vasarevičius
DOI: https://doi.org/10.3390/su16052106
IF: 3.9
2024-03-04
Sustainability
Abstract:This study conducted an in-depth examination of the delamination process of multi-layer packaging waste (MLPW) recycling, intending to find an effective solution for recycling MLPW. The recycling process for such materials can be challenging due to the complexity of separating the different layers and components. However, this study proposed using nitric acid to facilitate delamination and recover the polymers from multilayer food packaging—the research aimed to investigate the mechanical properties of the polymers obtained through this recycling method. Our study on polymer materials exposed to chemicals revealed differences in fracture and tensile strengths among three polymers, P1, P2, and P3. P1 showed fluctuating fracture strengths between 5.11 MPa and 3.55 MPa, while P2 maintained a consistent but lower value of around 0.09 MPa. P3 exhibited a wider range from 3.19 MPa to 1.79 MPa. Tensile strength analysis showed P1 averaging 4.99 MPa and P3 3.17 MPa, with P2's data inconclusive due to its softness. Understanding the mechanical characteristics of recycled polymers is crucial to determine their potential use in different industries, including packaging, construction, or manufacturing, thereby promoting a more environmentally friendly approach to MLPW management.
environmental sciences,environmental studies,green & sustainable science & technology
What problem does this paper attempt to address?
### What problem does this paper attempt to solve? This paper aims to explore an effective solution in the recycling process of multi - layer food packaging waste (MLPW). Specifically, the researchers propose to use nitric acid to promote the delamination of multi - layer packaging materials and recycle polymers from them. The main objectives of the paper are: 1. **Study the mechanical properties of recycled polymers**: Separate different layers in multi - layer food packaging by nitric acid and ultrasonic treatment, extract polymers, and analyze the mechanical properties of these polymers, such as tensile strength and breaking strength. 2. **Evaluate the application potential of recycled polymers**: Understanding the mechanical characteristics of these recycled polymers is crucial for determining their potential uses in different industries, including packaging, construction, and manufacturing. This helps promote more environmentally - friendly multi - layer food packaging waste management methods. 3. **Promote sustainable development**: Increase the recycling rate of multi - layer food packaging waste, reduce the impact on the environment, and promote the development of the circular economy. ### Specific research content - **Experimental design**: The researchers selected a specific type of multi - layer food packaging (such as potato chip packaging), cut it into strip - shaped samples of different widths, and carried out delamination experiments in nitric acid solutions of different concentrations. The experimental temperature, nitric acid concentration, sample width, and whether ultrasonic treatment was used were all key factors affecting the delamination effect. - **Mechanical property testing**: Use the standard "ASTM D882 - 18 Standard Test Method for Tensile Properties of Thin Plastic Sheeting" to test the mechanical properties of the recycled polymers. The test results show that there are significant differences in tensile strength and breaking strength among different polymers. - **Result analysis**: The study found that the breaking strength of polymer 1 (P1) fluctuated between 5.11 MPa and 3.55 MPa, while the breaking strength of polymer 2 (P2) was relatively stable, at about 0.09 MPa. The breaking strength range of polymer 3 (P3) was relatively wide, ranging from 3.19 MPa to 1.79 MPa. Tensile strength tests showed that the average tensile strength of P1 was 4.99 MPa, that of P3 was 3.17 MPa, and the data of P2 was unclear because the material was relatively soft. ### Conclusion Through this study, the authors hope to provide an effective method for the recycling of multi - layer food packaging waste and provide a scientific basis for the reuse of these recycled materials. This will not only help reduce environmental pollution, but also promote the recycling of resources and promote sustainable development.