Abstract:Objective:To assess the feasibility and safety of using a novel intravascular stent in clinical practice through animal experiment.Methods:Thirty intravascular stents prepared by metal powder injection molding were implanted into the aorta of 30 experimental dogs,respectively.After implantation,the intra-aortic conditions were observed by computed tomography angiography,and the neointimal formations on the stent surface at different postoperative times were observed by gross visual inspection and microscopic and electron microscopic evaluation as well as immunohistochemical staining.Results:All intravascular stents were successfully implanted into the aorta of the dogs.All stents were patent without any evidence of stent displacement,distortion or fracture and intrastent infection or thrombosis as well as intraluminal stenosis or occlusion;the longitudinal and radial shrinkage rates of the stents were less than 2％ and 4％,respectively.At one week after implantation,the luminal surface of the stent was rapidly covered by a thin layer of semi-transparent membrane-hke structure;at one month after implantation,neointimal formations were seen on most of the luminal surface of the stent which connected with the surrounding intima;at 2 months after implantation,nearly the complete luminal surface of the stent (98.83％) was covered by the neointima,and its thickness reached a peak value (350.00 μn);at 3 to 6 months after implantation,the thickness of the neointima was gradually reduced,its inside diameter was gradually increased to almost the initial size before implantation,and finally,the neointimal surface was covered by a single layer of fully mature endothelial cells.In the neointimal tissues on the luminal surface of the stent,positive staining of smooth muscle α-actin was detected at each time point except one week after immplantaion,while positive staining of vascular endothelial growth factor was detected at any time point aer immplantaion.Conclusion:Ihe novel intravascular stent prepared by metal powder injection molding can maintain stable form and structure with fast endothelialization of the luminal surface of stent,and keep long-term patency.It shows favorable structural,physical and chemical stability and biocompatibility and may have a promising application prospect in clinical practice.

Biocompatibility of vascular stents manufactured using metal injection molding in animal experiments

Application of a novel intravascular stent prepared by metal powder injection molding in animals

Computational biomechanics and experimental verification of vascular stent

Study on Biocompatibility of MIM 316L Stainless Steel

Fabrication of Nonbiofouling Metal Stent and in Vitro Studies on Its Hemocompatibility

Comparison of Modified Injection Molding and Conventional Machining in Biodegradable Behavior of Perforated Cannulated Magnesium Hip Stents

A biodegradable metal‐polymer composite stent safe and effective on physiological and serum‐containing biomimetic conditions

Biocompatibility of Surface Magnetic Film Medical 316L Stainless Steel Stent in Vivo

3D Printing and Characterization of the Biodegradable Vascular Stent

Additive Manufacturing of Biodegradable Molybdenum – From Powder to Vascular Stent

Covalent Immobilization of Biomolecules on Stent Materials Through Mussel Adhesive Protein Coating to Form Biofunctional Films.

Experimental Novel Absorbable Magnesium Alloy Stent

[The in Vivo Thrombosis Evaluation for the Biodegradable Polymer Stent].

Optimized design and biomechanical evaluation of biodegradable magnesium alloy vascular stents

Enhanced in Vitro and in Vivo Performance of Mg-Zn-Y-Nd Alloy Achieved with Aptes Pretreatment for Drug-Eluting Vascular Stent Application

The Studies on Biocompatibility of Self-Expanding Niti Stent and Apoptosis of Smooth Muscle Cells after Stenting

Evaluation of Promoting Effect of a Novel Cu-bearing Metal Stent on Endothelialization Process from in Vitro and in Vivo Studies

Mechanical Analysis of New Type Biodegradable Metal Stents Based on FEM

Past and Recent Progress on Metallic Digestive Tract Stents

The Process and Performance of Endovascular Stents

Long-Term Efficacy of Biodegradable Metal-Polymer Composite Stents after the First and the Second Implantations into Porcine Coronary Arteries