Abstract:The mass loss kinetics of thermally modified wood species was analyzed as a time–temperature function. European beech (Fagus sylvatica L.), English oak (Quercus robur L.), Norwegian spruce (Picea abies L. Karst.) and Scots pine (Pinus sylvestris L.) wood specimens of dimensions 20 × 20 × 10 mm3 were thermally modified at 140 °C, 160 °C, 180 °C, 200 °C and 220 °C for 1–6 h using atmospheric pressure and superheated steam environment. The process intensity was determined by mass loss (ML), based on oven-dry mass before and after the thermal modification. Furthermore, the equilibrium moisture content (EMC) was determined before and after thermal modification to analyze the effect of mass loss on the sorption properties. Measured mass loss data were compared with the three-dimensional analytical function and its applicability to mass loss prediction was verified. For the studied wood species, the ML was found to be less than 1–1.5% when temperature of 140 °C and 160 °C was applied. Differences between studied species were more significant at temperatures higher than 160 °C. With the highest tested temperature (220 °C), mass loss reached 13.5% (beech), 18.8% (oak), 6.7% (spruce) and 13.5% (pine). According to the results, hardwoods have been shown to be more sensitive to the thermal degradation than softwoods as demonstrated by the higher mass loss recorded for the same modification time and temperature. The three-dimensional analytical function was confirmed as valid for all the species studied (R2 = 0.89–0.99) and relevant for the mass loss prediction using fitted parameters. The EMC was reduced after thermal modification within the range of 4–48%, 0.4–47%, 1–32% and 0.7–40% for beech, oak, spruce and pine, respectively. Further, the EMC correlates exponentially (R2 = 0.91–0.95) with the decrease in the specimens' mass depending on the wood species used and modification temperature applied. However, the EMC seems to be almost stabilized beyond a limit value of approximately 10–12% of mass loss. The results provide a better insight into the mass loss and EMC kinetics of thermally modified wood species and can be used as a tool for prediction of mass loss values and required material properties (EMC) for designed wooden products.

Thermophysical Properties of Beech Wood in the Range from Room Temperature to 900 °C

Specific heat capacity of wood between −140 and 50 °C in dry and wet state

Physical, mechanical, and thermal properties of heat-treated poplar and beech wood

The compressive behaviour of beech and birch at different moisture and temperature conditions along the grain

Characterisation of thermally treated beech and birch by means of quasi-static tests and ultrasonic waves

Chemical changes in thermally modified, acetylated and melamine formaldehyde resin impregnated beech wood

Viscoelastic properties of wood across the grain measured under water-saturated conditions up to 135\degree C: evidence of thermal degradation

The vibrational properties of native and thermally modified wood in dependence on its moisture content

Measurements of the mechanical properties of larch at elevated and high temperature under nitrogen conditions

Experimental Study of the Anisotropic Thermal Conductivity of Spruce Wood

Mass loss kinetics of thermally modified wood species as a time–temperature function

Thermal Responses of Woods Exposed to High Temperatures Considering Apparent Thermo-Physical Properties

Swelling kinetics of thermally modified wood

Mild hydrothermal modification of beech wood (Zelkova schneideriana Hand-Mzt): its physical, structural, and mechanical properties

Exploratory study on the bending performance of thermo-hydro-mechanically densified Scots pine (Pinus sylvestris L.) at elevated temperatures

The Influence of Drying Temperature on Color Change of Hornbeam and Maple Wood Used as Surface and Inner Layers of Wood Composites

Effect of High-Temperature Paraffin Impregnation on the Properties of the Amorphous Cellulose Region Based on Molecular Dynamics Simulation

Long-Term Hygroscopic Thickness Swelling Rate of Hydrothermally Treated Beech Wood / Polypropylene Composites

Thermal properties of wood: measurements by transient plane source method in dry and wet conditions

Influence of thermo-vacuum treatment on thermal degradation of various wood species

Thermal degradation mechanisms of wood under inert and oxidative environments using DAEM methods