Mild hydrothermal modification of beech wood (Zelkova schneideriana Hand-Mzt): its physical, structural, and mechanical properties

Wu, Zhihui

DOI: https://doi.org/10.1007/s00107-022-01805-7

2022-03-25

Abstract:Wood modification at a high temperature (180–300 °C) and duration (> 5 h) consumes energy and results in a decrease in the quality of the wood. Therefore, wood modifications at mild temperature (120–180 °C) within a short duration (1–5 h) are proposed to improve dimensional stability, hardness, and flexural modulus with consideration of the wood applications and consumption during manufacturing. The effect of the temperature and duration of mild hydrothermal modification on the properties of beech wood ( Zelkova schneideriana Hand-Mzt) was investigated in this study. The physical and mechanical properties of modified wood were measured. Scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray diffraction were used to analyze the morphology, chemical composition, and crystallinity of modified wood, respectively. The mechanical properties of the wood were deteriorated at high temperatures (180 °C) and durations (5 h). At a temperature of 140–160 °C and duration of 3 h, a moderate increase and decrease were found in dimensional stability and mechanical properties of modified wood, respectively, and the integrated properties of the wood were acceptable. Therefore, mild hydrothermal modifications can be applied into wood modification to obtain improved dimensional stability, good surficial appearance, and almost unchanged mechanical properties that are needed in practical building materials, such as furniture production, and to maximize the functional efficiency and industrial production benefits of wood modification.