Abstract:Wood is one of the most popular materials for construction purposes because of its environmentally friendly and sustainable characteristics. However, the use of wood is constrained by the lengthy time it takes for trees to mature. Consequently, fast-growing wood species have become popular as substitute options due to their ability to rapidly reach maturity and high yields. Although the problem of low density and strength has been effectively addressed in recent years by densifying wood, the problem of large thickness swelling due to moisture and water absorption has limited its application. Therefore, we reported an effective modification strategy to overcome the thickness swelling issue of densified wood by preparing a cellulosic reinforced material through the synergistic action of alkaline chemical pretreatment, multi-step cyclic impregnation and high-temperature densification. The results showed that the alkaline chemical pretreatment was effective for removing a large amount of lignin and hemicelluloses, creating a large number of hydrogen bonds among the remaining strong celluloses. The impregnated sodium silicate solution bonded celluloses tightly, and the densification treatment contributed to the production of Si-O-Si structure, forming the shuttle hybridized structure through Si-O-C bonds. The hardness, flexural strength, elastic modulus , and compressive strength of the modified wood increased by 3.9, 6.0, 3.4 and 28.2 times, respectively. In addition, 0 % thickness swelling for 30-day moisture absorption and 1.0 % thickness swelling for 72-hour water absorption were achieved, realizing super dimensional-stable poplar structures. Furthermore, the high-performance densified wood prepared by this method has excellent fire and mildew resistance properties, which lays the foundation for the application of fast-growing wood in outdoor engineering structures.

Ultra-High-Pressure Modification of Wood: Densification and Dyeing

High-Pressure Treatment of Chinese Fir Wood: Effect on Density, Mechanical Properties, Humidity-Related Moisture Migration, and Dimensional Stability

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Plastic and Elastic Strains in Poplar Wood under High-Pressure Densification

Dyeing of Poplar Wood Through High-Pressure Processing: Performance Evaluation

Effect of High-pressure Densification on Moisture Sorption Properties of Paulownia Wood

Effect of superheated steam pressure on the physical and mechanical properties of sandwich-densified wood

Optimization of mechanical properties and dimensional stability of densified wood using response surface methodology

High-Pressure Treatment Effects on Density Profile, Surface Roughness, Hardness, and Abrasion Resistance of Paulownia Wood Boards

Research Progress of Reinforced Modification of Fast-Growing Wood

Production processes, material properties and applications of densified wood: an overview

Application of High Pressure Processing on Fast-growing Chinese Fir

Integrated approach for improving mechanical and high-temperature properties of fast-growing poplar wood using lignin-controlled treatment combined with densification

Improvement of decorative texture effects, thermal stability, and mechanical properties of Pinus massoniana using a combined dyeing and superhydrophobic modification method

Fabrication of High-Performance Densified Wood via High-Pressure Steam Treatment and Hot-Pressing

Characterization of Microstructure, Chemical, and Physical Properties of Delignified and Densified Poplar Wood

Development of super dimensional stable poplar structure with fire and mildew resistance by delignification/densification of wood with highly aligned cellulose molecules

Manufacturing and Characterization of Modified Wood with In Situ Polymerization and Cross-linking of Water-Soluble Monomers on Wood Cell Walls

Effects of chemical modification and nanotechnology on wood properties

Green and sustainable fabrication of DES-pretreated high-strength densified wood