Abstract:Fresh martensite (FM) is often present in medium-Mn steels, especially when containing lower Mn content, due to the insufficient thermal stability of reverted austenite; this FM is brittle, largely deteriorating the ductility. In this paper, large ductility and high yield strength are achieved in an Al/Si-added medium-Mn steel containing 2.7Mn via a two-step partitioning heat treatment, i.e. intercritical annealing (IA) followed by low-temperature partitioning (LTP). We show that, during the IA, C and Mn atoms partition from the pre-quenched martensite to reverted austenite; Al addition reduces the size of reverted austenite and promotes C and Mn enrichment in the reverted austenite by decelerating its growth kinetics. This enables the reverted austenite more thermally stabilized, thereby reducing the amount of FM and increasing the amount and mechanical stability of retained austenite (RA) at room temperature. During the LTP, accompanied with the recovery of dislocations and the suppression of carbide precipitation by Al and Si, C atoms further partition from FM to RA, which enables the RA more mechanically stabilized and thereby sustains the high strain hardening to larger strains. Simultaneously, the FM becomes less hard and less brittle due to C atoms depletion and dislocations recovery, alleviating the stress/strain localization and favoring the uniform plastic deformation. Furthermore, the decrease in mobile dislocation density that is accompanied with the recovery of dislocations is believed to be mainly responsible for the enhanced yield strength of the steel. The present results indicate that the synergetic effects of the primary element partitioning (promoted by Al) during IA, which increases the thermal stability of reverted austenite, and the secondary element partitioning (enhanced by Al and Si) and as well dislocation recovery during LTP, which increases the mechanical stability of RA and the uniformity of plastic deformation, significantly enhance both the ductility and yield strength of medium-Mn steel with low Mn content.

Stabilizing austenite via intercritical Mn partitioning in a medium Mn steel

Stabilizing Austenite Via a Core-Shell Structure in the Medium Mn Steels

Tailoring the metastable reversed austenite from metastable Mn-rich carbides

Improving the Ductility of Ultrahigh-Strength Medium Mn Steels Via Introducing Pre-Existed Austenite Acting As a "reservoir" for Mn Atoms

High strength and ductility combination in nano-/ultrafine-grained medium-Mn steel by tuning the stability of reverted austenite involving intercritical annealing

Mechanistic role of Mn heterogeneity in austenite decomposition and stabilization in a commercial quenching and partitioning steel

C and Mn Elements Characterization and Stability of Retained Austenite in Different Locations of Quenching and Partitioning Bainite Steels

New observations of the twinning effect and austenite stability in intercritical quenched and tempered steel with high strength

Formation of core-shell austenite as promoted by alloying solutes in hot-rolled medium Mn steel

Strong and ductile medium manganese steel processed by low-temperature partitioning

A Cyclic Austenite Reversion Treatment for Stabilizing Austenite in the Medium Manganese Steels

The influence of cooling methods on the austenite stability and plastic instability behavior in 3Mn steel

Austenite Thermal Stabilization Through the Concentration of Manganese and Carbon in the 0.2c–5mn Steel

Enhancing the ductility and yield strength of 2.7Mn steel via two-step partitioning heat treatment

Enhancing the Hydrogen Embrittlement Resistance of Medium Mn Steels by Designing Metastable Austenite with a Compositional Core–shell Structure

Kinetic Transitions and Mn Partitioning During Austenite Growth from a Mixture of Partitioned Cementite and Ferrite: Role of Heating Rate

Heterogeneous Multiphase Microstructure Formation through Partial Recrystallization of a Warm-Deformed Medium Mn Steel during High-Temperature Partitioning

Effect of Intercritical Dislocation Multiplication to Mn Partitioning and Microstructure Evolution of Bainite in Low Carbon Steel

Austenite Formation and Cementite Dissolution During Intercritical Annealing of a Medium-Manganese Steel from a Martensitic Condition

Tailoring hetero-grained austenite via a cyclic thermomechanical process for achieving ultrahigh strength-ductility in medium-Mn steel

Heterostructure mediated high strength and large ductility in novel medium-Mn steels with low Mn content