Low-loss Cd-substituted Mg ferrites with matching impedance for high-frequency-range antennas
Gongwen Gan,Dainan Zhang,Jie Li,Gang Wang,Xin Huang,Yan Yang,Yiheng Rao,Xueying Wang,Huaiwu Zhang,Ray T. Chen
DOI: https://doi.org/10.1016/j.jma.2020.09.007
IF: 11.813
2020-10-01
Journal of Magnesium and Alloys
Abstract:The effects of Cd<sup>2+</sup> ions on the microstructure, magnetic properties, and dielectric properties of Bi<sub>2</sub>O<sub>3</sub>-added MgFe<sub>2</sub>O<sub>4</sub> ferrites (Cd<sub>x</sub>Mg<sub>1-x</sub>Fe<sub>2</sub>O<sub>4</sub>, <em>x</em> = 0.00, 0.15, 0.30 and 0.45) are obtained by adopting the solid-state reaction method at a low temperature (910 °C). The objective is to achieve matching impedances, low magnetic and dielectric losses (tan <em>δ<sub>μ</sub></em> and tan <em>δ<sub>ε</sub></em>, respectively), and a relatively large miniaturization factor to reduce antenna size. Experimental results indicate that the cations occupying the tetrahedral (A) and octahedral (B) ion sites are redistributed, resulting in an enhanced super-exchange interaction between the two sublattices. As a result, improved magnetization, including the increase in saturation magnetization (41.74 emu/g) and decrease in coercivity (63.75 Oe), is realized. The real part of permeability (µ<em>′</em>) also increases with increasing concentration of Cd<sup>2+</sup> ions. When x is 0.15, matching impedances with equivalent <em>μ′</em> and <em>ε′</em> values are obtained over a long frequency range (1–150 MHz). Moreover, the formation of a dense microstructure guarantees that losses occur at low orders of magnitude (tan <em>δ<sub>μ</sub></em> ≈ 10<sup>−2</sup> and tan <em>δ<sub>ε</sub></em> ≈ 10<sup>−3</sup>). Accordingly, these properties afford wide application perspectives for the proposed compounds in the high-frequency region, i.e., from high-frequency to very-high-frequency bands.
metallurgy & metallurgical engineering