Abstract:Surface preparation of ultra-high modulus fiber composites for adhesive bonding is challenging due to the subsurface damages that can occur during a standard abrasion operation that could weaken the laminate cohesion. Therefore, it is highly desirable to utilize a non-contact method that can clean and activate the composite surface without exerting an external force to eliminate potential damage. This investigation focuses on the use of atmospheric plasma treatment (APT) for the surface preparation of unidirectional ultra-high modulus, composites for adhesive bonding. The laminates were manufactured using Mitsubishi K13C2U pitch-based carbon fiber with Tencate's RS-3C cyanate-ester resin and bonded with Henkel 9394 epoxy. Surface analysis of plasma-treated samples revealed a significant reduction of surface contamination and increased chemical modification of the matrix material resulting in improved wetting and the formation of chemical groups conducive to bonding. The plasma treatment also produced a minor increase in surface roughening, well below levels expected to contribute to mechanical interlocking. APT epoxy-bonded lap-shear specimens (LSS) exhibited a 50% increase in strength as compared to mechanically abraded samples. It was also shown that solvent rinsing after APT removed a highly-oxidized, poorly bonded carbonate component from the treated resin surface as evidenced by XPS. This surface ash is observed at fairly high concentrations after APT of cyanate ester resin composites limiting functional group contributions. The removal of this ash resulted in increases in LSS of 25% as compared to unrinsed APT surfaces. Lap shear strengths and GIC delamination resistance tests showed improvements over abrasion surface treated samples. Image analysis of the fracture faces for both surface treatments showed that abrasion treated surfaces resulted in sub-surface damage to the fibers that translated into brittle fracture through weak, highly aligned layers within these graphitic fibers. On the other hand, plasma treatment was successfully applied to minimize subsurface damage and resulted in crack propagation along with the more tortuous fiber-matrix interface. The degree of the improvements was ultimately limited by the interlaminar strength of these composites.

Surface grafting modification of carbon fibers by γ-ray pre-irradiation and plasma technique

Effect of Irradiation Grafting Epoxy on Surface Characteristics of Carbon Fibers and Mechanical Properties of Composites

Enhancing CFRP Laminates with Plasma Jet Arrays: A Study of Interlaminar Mechanical Properties

Surface modification of PVDF porous membranes by electron irradiation

Effects of carbon fibers modification on the properties of unsaturated polyester self-healing composites

Effect of Γ-Ray Irradiation Grafting on the Surface Property and the Bulk Structure of M40J Fiber

Grafting Onto the Surface of Plasma-Modified Fillers

Reinforcement of carbon fibers: γ-irradiation induced microporous modulation and surface defect repairing with graphene quantum dots

Surface Modification of Poly(tetrafluoroethylene) Films Via Plasma Treatment and Graft Copolymerization of Acrylic Acid

Improving the interfacial property of carbon fiber/PI resin composite by grafting modification of carbon fiber surface

Structure transformation and interfacial properties enhancement of high-strength carbon fibers (T800) grafted by glycidyl methacrylate via heat treatment synergized with ionizing radiation

Improving the Mechanical and Surface Properties of Aramid Fiber by Grafting with 1,4-Dichlorobutane under Supercritical Carbon Dioxide

Rapid and Continuous Atmospheric Plasma Surface Modification of PAN-Based Carbon Fibers

Improved mechanical properties of carbon fiber/epoxy composites via fiber surface grafting of rigid-flexible chain structure

Improving the interfacial property of carbon fiber/vinyl ester resin composite by grafting modification of sizing agent on carbon fiber surface

Carbon Fiber Surface Modification by Plasma Treatment for Interface Adhesion Improvements of Aerospace Composites

Study on Surface Properties of Aramid Fiber Modified in Supercritical Carbon Dioxide by Glycidyl-POSS

Impact of plasma-modified pretreatment on the tensile properties of carbon fiber-reinforced epoxy composites

Investigations on the effect of plasma treatment on the adhesive bonding behavior of ultra high modulus K13C2U/cyanate ester fiber composites

Optimization of Surface Modification Process of Kevlar Fabric by Ar Plasma for Improvement of Adhesion to Epoxy Matrices

Surface Modification and Adhesion Improvement of Expanded Poly(tetrafluoroethylene) Films by Plasma Graft Polymerization