Abstract:This study describes the effect of heat treatment on some physical, chemical, and mechanical properties of Eucalyptus Camaldulensis (EC) wood at different temperatures and treatment times (200 °C-260 °C for 5, 60, and 90 min). The evaluation of hygroscopic properties was determined by relative humidity, mass loss, dimensional stability tests, and density. The results showed that the heat treatment leads to an increase in mass loss of 5.2 %-11.9 % at 200 °C. The density changed significantly for this studied species as well as the dimensional stabilization. Chemical changes in wood structure were assessed by Fourier Transform Infrared Spectroscopy.To verify the validity of the superposition "Mass loss-Density-water absorption" on the mechanical properties (modulus of elasticity (MOE) and modulus of rupture (MOR)) during heat treatment, we have developed a mathematical model based on Multiple Linear Regression (MLR), in order to establish a relationship between the independent parameters and the dependent parameters (MOE and MOR). The evaluation of the quality of the models developed was based on several statistical tools, namely R = 0.99, R2 = 0.99, R2adj = 0.98, and F = 132.33. The results demonstrated that elaborate models of mechanical properties have a high predictive capacity (MOR and MOE). The wood's carbohydrates (particularly hemicelluloses) are then degraded during the heat treatment. The % of carbon increases from 47.8 to 49.8 %, which is proportional to mass loss, while the % of oxygen decreases by 46.1 %, which is inversely proportional to mass loss. Furthermore, FTIR analysis revealed that the effect of heat-treated wood chemical changes was related to the hydroxyl OH function of cellulose, functional groups, and aromatic system of lignin. In conclusion, the results demonstrated that at 200 °C, heat treatment caused a 5.2-11.9 % increase in mass loss; dimensional stability and density underwent considerable changes. FTIR spectroscopy confirmed the chemical changes in the wood structure during heat treatment. Furthermore, the "MLR" mathematical model showed that density contributed to the increase in MOR and MOE properties, while water absorption and mass loss contributed to the decrease in MOR and MOE properties. Finally, the % of oxygen decreased by 46.1 %, which is inversely proportional to the loss of mass, and the % of carbon increased from 47.8 % to 49.8 %, which is proportional to the loss of mass.

Influence of habitat, density, lignin structure, and extraction treatment on thermal-softening properties of water-swollen wood: a study of 87 wood specimens

Viscoelastic properties of wood across the grain measured under water-saturated conditions up to 135\degree C: evidence of thermal degradation

Evaluation of the Colour Parameters on Hygroscopicity and Dimensional Stability of Thermally Modified Populus Tomentosa Carr.

Effects of water-soluble extractives on the vibrational properties and color of hygrothermally treated spruce wood

Effect of a Combination of Moderate-Temperature Heat Treatment and Subsequent Wax Impregnation on Wood Hygroscopicity, Dimensional Stability, and Mechanical Properties

In Situ Micro-Ftir Observation of Molecular Association of Adsorbed Water with Heat-Treated Wood

Effects of Heat Treatment on Some Physical Properties of Douglas Fir (pseudotsuga Menziesii) Wood

Temperature and time dependence of orthotropic viscoelastic properties of moist wood determined in tensile mode

Moisture transport dynamics in wood during drying studied by long-wave near-infrared hyperspectral imaging

Viscoelastic properties of green wood across the grain measured by harmonic tests in the range of 0\degree C to 95\degree C. Hardwood vs. softwood and normal wood vs. reaction wood

Effect of thermal treatment with water, H2SO4 and NaOH aqueous solution on color, cell wall and chemical structure of poplar wood

Establishment of moisture diffusion regularities through the polymer shell of thermally modified wood

Effects of different heat treatment media on odorous constituents, chemical decomposition and mechanical properties of two hardwoods

Impact on Timber Crystallization Performance of Superheated Steam-Treated Wood under High Temperature and Pressure

Effects of Drying Temperature on Hygroscopicity and Mechanical Performance of Resin-Impregnated Wood

Experimental Measurements of Thermal Conductivity of Wood Species in China: Effects of Density, Temperature, and Moisture Content

Effects of thermal modification on the mechanical properties of the wood cell wall of soft wood: behavior of S2 cellulose microfibrils under tensile loading

Mechanical properties of industrial heat-treated wood

Effects of the ice formation and its content on viscoelastic characteristics of wood exposure to low temperatures ranging from −125°C to 25°C

Study of the effect of heat temperature on the chemical changes and hygroscopicity of eucalyptus wood by FT-IR and prediction of mechanical properties by the MLR regression method

Swelling kinetics of thermally modified wood