Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Mechanisms of failure under low cycle fatigue, high cycle fatigue and creep interactions in combined cycling in a type 316LN stainless steel

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Influence of Prior Low Cycle Fatigue on Microstructure Evolution and Subsequent Creep Behavior

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Remaining creep properties and fracture behaviour of P92 steel welded joint under prior low cycle fatigue loading

The correlation between prior fatigue damage and remaining creep properties in a high chromium steel welded joint

Effect of hold-time on low cycle fatigue behaviour of nitrogen bearing 316L stainless steel

Experimental and constitutive modelling studies of type 316L stainless steel based on internal stress under low cycle fatigue and creep-fatigue interaction

Life prediction and damage analysis of creep-fatigue combined with high-low cycle loading by using a crystal plasticity-based approach

A Modified Microstructure-Based Creep Damage Model for Considering Prior Low Cycle Fatigue Damage Effects

Creep-fatigue Properties and Deformation Mechanism of 316L Steel Fabricated by Laser Powder Bed Fusion (PBF-LB/M)

Characterization of the Cyclic Softening and Remaining Creep Behaviour of P92 Steel Weldment

Low cycle fatigue behavior of 316LN stainless steel: Effects of temperature, strain rate and strain amplitude

Influence of time and temperature dependent processes on strain controlled low cycle fatigue behavior of alloy 617

Revealing the influential mechanism of strain ranges on cyclic-life saturation during creep-fatigue in Nickel-based superalloy DZ445

A creep damage model for low cycle fatigue based on the equivalent creep stress: Establishment, verification and application

Cyclic Deformation and Low-Cycle Fatigue for 316LN Stainless Steel under Non-proportional Loading

Analysis of high temperature and strain amplitude effects on low cycle fatigue behavior of pitting corroded killed E350 BR structural steel