Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Effect of hold-time on low cycle fatigue behaviour of nitrogen bearing 316L stainless steel

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

The Effect of Nitrogen Alloying on the Low Cycle Fatigue and Creep-Fatigue Interaction Behavior of 316LN Stainless Steel

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Effects of temperature on the low cycle fatigue behaviour of nitrogen alloyed type 316L stainless steel

Effect of nitrogen on high temperature low cycle fatigue behaviors in type 316L stainless steel

Effect of strain rate on low cycle fatigue of 316LN stainless steel with varying nitrogen content: Part-II fatigue life and fracture

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Creep–fatigue interaction behavior of 316LN austenitic stainless steel with varying nitrogen content

Low cycle fatigue behavior of 316LN stainless steel: Effects of temperature, strain rate and strain amplitude

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Effect of strain rate on low cycle fatigue of 316LN stainless steel with varying nitrogen content: Part-I cyclic deformation behavior

Mechanisms of failure under low cycle fatigue, high cycle fatigue and creep interactions in combined cycling in a type 316LN stainless steel

Low Cycle Fatigue Behavior of 316LN Stainless Steel Alloyed with Varying Nitrogen Content. Part I: Cyclic Deformation Behavior

Effects of Dwell Time on the Isothermal and Thermomechanical Fatigue Behavior of 316LN Stainless Steel

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Creep-fatigue Properties and Deformation Mechanism of 316L Steel Fabricated by Laser Powder Bed Fusion (PBF-LB/M)

Influence of Prior Low Cycle Fatigue on Microstructure Evolution and Subsequent Creep Behavior