Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

The Effect of Nitrogen Alloying on the Low Cycle Fatigue and Creep-Fatigue Interaction Behavior of 316LN Stainless Steel

Effect of strain rate on low cycle fatigue of 316LN stainless steel with varying nitrogen content: Part-II fatigue life and fracture

Creep–fatigue interaction behavior of 316LN austenitic stainless steel with varying nitrogen content

Strain controlled fatigue deformation and fracture of nitrogen alloyed 316LN austenitic stainless steel

Low Cycle Fatigue Behavior of 316LN Stainless Steel Alloyed with Varying Nitrogen Content. Part II: Fatigue Life and Fracture Behavior

Influence of nitrogen alloying on dynamic strain ageing regimes in low cycle fatigue of AISI 316LN stainless steel

Low Cycle Fatigue Behavior of 316LN Stainless Steel Alloyed with Varying Nitrogen Content. Part I: Cyclic Deformation Behavior

Effect of strain rate on low cycle fatigue of 316LN stainless steel with varying nitrogen content: Part-I cyclic deformation behavior

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Low-temperature fatigue of 316L and 316LN austenitic stainless steels

Effect of hold-time on low cycle fatigue behaviour of nitrogen bearing 316L stainless steel

Effect of nitrogen on high temperature low cycle fatigue behaviors in type 316L stainless steel

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Influence of Secondary Cyclic Hardening on the Low Cycle Fatigue Behavior of Nitrogen Alloyed 316LN Stainless Steel

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Creep strengthening of low carbon grade type 316LN stainless steel by nitrogen

Low cycle fatigue behavior of 316LN stainless steel: Effects of temperature, strain rate and strain amplitude

Effects of temperature on the low cycle fatigue behaviour of nitrogen alloyed type 316L stainless steel

On the Relationship Between Cyclic Deformation Behavior and Slip Mode in 316LN Stainless Steel with Varying Nitrogen Content