Creep strengthening of low carbon grade type 316LN stainless steel by nitrogen

V. Ganesan,M. D. Mathew,P. Parameswaran,K. Bhanu Sankara Rao

DOI: https://doi.org/10.1007/s12666-010-0057-2

2010-04-01

Transactions of the Indian Institute of Metals

Abstract:Nitrogen-alloyed 316LN stainless steel is used as a structural material for high temperature fast breeder reactor components. With a view to increase the design life of the components up to 60 years and beyond, studies are being carried out to develop nitrogen alloyed 316LN stainless steel with superior tensile, creep and low cycle fatigue properties. This paper presents the results from studies on the influence of nitrogen on the high temperature creep properties of this material. The influence of nitrogen on the creep behaviour of 316LN stainless steel has been studied at nitrogen levels of 0.07, 0.11, 0.14 and 0.22 wt%. Creep tests were carried out at 923 K at stress levels 140, 175, 200 and 225 MPa. Creep rupture strength increased substantially with increase in nitrogen content. The variation of steady state creep rate with stress showed a power law relationship. The power law exponent varied between 6.4 and 13.7 depending upon the nitrogen content. Rupture ductility was generally above 40% at all the test conditions and for all the nitrogen contents. It was observed that the internal creep damage and surface damage decreased with increase in nitrogen content. Fracture mode was found to generally shift from intergranular failure to transgranular failure with increasing nitrogen content.

metallurgy & metallurgical engineering