Abstract:Arsenite (As(III)) is more toxic and more difficult to remove from water than arsenate (As(V)). As there is no simple treatment for the efficient removal of As(III), an oxidation step is always necessary to achieve higher removal. However, this leads to a complicated operation and is not cost-effective. To overcome these disadvantage, a novel Fe–Mn binary oxide material which combined the oxidation property of manganese dioxide and the high adsorption features to As(V) of iron oxides, were developed from low cost materials using a simultaneous oxidation and coprecipitation method. The adsorbent was characterized by BET surface areas measurement, powder XRD, SEM, and XPS. The results showed that prepared Fe–Mn binary oxide with a high surface area (265m2g-1) was amorphous. Iron and manganese existed mainly in the oxidation state +III and IV, respectively. Laboratory experiments were carried out to investigate adsorption kinetics, adsorption capacity of the adsorbent and the effect of solution pH values on arsenic removal. Batch experimental results showed that the adsorbent could completely oxidize As(III) to As(V) and was effective for both As(V) and As(III) removal, particularly the As(III). The maximal adsorption capacities of As(V) and As(III) were 0.93mmolg-1 and 1.77mmolg-1, respectively. The results compare favorably with those obtained using other adsorbent. The effects of anions such as SO42-, PO43-, SiO32-, CO32- and humic acid (HA), which possibly exist in natural water, on As(III) removal were also investigated. The results indicated that phosphate was the greatest competitor with arsenic for adsorptive sites on the adsorbent. The presence of sulfate and HA had no significant effect on arsenic removal. The high uptake capability of the Fe–Mn binary oxide makes it potentially attractive adsorbent for the removal of As(III) from aqueous solution.

Efficient removal of arsenic by electrodeposited CuFeOx foam

Highly Porous Copper Ferrite Foam: A Promising Adsorbent for Efficient Removal of As(III) and As(V) from Water.

Graphene Oxide/cufe2o4 Foam As an Efficient Absorbent for Arsenic Removal from Water

Arsenic Removal in Synthetic Ground Water Using Iron Electrolysis

[Arsenic Adsorption by Magnetic Adsorbent CuFe2O4].

Self-enhanced and Efficient Removal of As(III) from Water Using Fe–Cu–Mn Composite Oxide under Visible-Light Irradiation: Synergistic Oxidation and Mechanisms

Efficient As(III) Removal by Magnetic CuO-Fe3O4 Nanoparticles Through Photo-Oxidation and Adsorption under Light Irradiation

3D composite carbon Foam-Loaded MnO 2 and FeOOH enabling the "oxidation-adsorption" effect toward efficient removal of arsenic from groundwater

Cu doped Fe3O4 magnetic adsorbent for arsenic: synthesis, property, and sorption application

Removal Of Arsenic(Iii) From Aqueous Solution Using A Low-Cost By-Product In Fe-Removal Plants-Fe-Based Backwashing Sludge

Fast and Efficient Removal of As(III) from Water by CuFe2O4 with Peroxymonosulfate: Effects of Oxidation and Adsorption.

Facile Synthesis of Fe3O4@Cu(OH)2 Composites and Their Arsenic Adsorption Application

Removal of arsenic(v) from aqueous solutions using sulfur-doped Fe3O4 nanoparticles.

Enhanced removal of As (V) from aqueous solution using modified hydrous ferric oxide nanoparticles

Rapid purification of As(III) in water using iron-manganese composite oxide coupled with sulfite: Importance of the SO5?- radicals

Preparation and Evaluation of a Novel Fe–Mn Binary Oxide Adsorbent for Effective Arsenite Removal

Arsenic removal from water by nanometer iron oxide coated single-wall carbon nanotubes

Removal of arsenic(V) from aqueous solutions using iron-oxide-coated modified activated carbon.

A Novel Nanostructured Fe-Ti-Mn Composite Oxide for Highly Efficient Arsenic Removal: Preparation and Performance Evaluation

Superparamagnetic high-surface-area Fe 3O 4 nanoparticles as adsorbents for arsenic removal

Fesx@Mof-808 Composite for Efficient As(Iii) Removal from Wastewater: Behavior and Mechanism