Abstract:The stainless-clad (SC) bimetallic steel that is manufactured by metallurgically bonding stainless steels as cladding metal and conventional mild (CM) steel as substrate metal, is a kind of advanced steel with low cost, high strength and outstanding corrosion-resistant performance. Such advanced steels are especially competitive in the application of engineering structures with demands of high corrosion resistance. Unfortunately, the cyclic behaviour of the SC bimetallic steel is different from that of CM steel or stainless steel, and the research work on the SC bimetallic steels from material level to structural design level for the applications in structural engineering field is very limited. Therefore, this paper aims to investigate the low-cycle fatigue behaviour of the SC bimetallic steel made by hot roll bonding of austenitic stainless steel (S31603) and CM steel (Q355B). The test adopted a constant strain amplitude cyclic loading system with strain ratios of -1 and 0, a strain rate of 0.5%.s(-1) and strain amplitudes varying from 1.00% to 2.50%. The fracture feature, cyclic characteristic, stress-strain response and the influence of surface defect and strain rate are analysed herein, and the strain-fatigue life curves are fitted and predicted by adapting the Basquin-Coffin-Manson model and Kuroda model. Research outcomes show that the introduction of cladding steel could significantly improve its ductility and low-cycle fatigue life; the fatigue life of the SC bimetallic steel is generally 30% similar to 60% higher compared with the corresponding CM steel, indicating its excellent low-cycle fatigue behaviour. The low-cycle fatigue life of the two steels could be well predicted by the strain-life relationship with adapted Basquin-Coffin-Manson model and Kuroda model, and the former is indicated superior to the latter in terms of the essential meaning and applicability.

High-cycle and very-high-cycle fatigue behavior of a stainless steel for air-conditioning compressor valve plates

High-cycle and very-high-cycle fatigue behavior of a stainless steel for air-conditioning compressor valve plates

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Fatigue hardening/softening behaviour investigated through Vickers microhardness measurement during high-cycle fatigue

A Study of the Back Stress and the Friction Stress Behaviors of Ti-6Al-4V Alloy During Low Cycle Fatigue at Room Temperature

Design Fatigue Life Evaluation of High-Pressure Hydrogen Storage Vessels Based on Fracture Mechanics

Very High Cycle Fatigue Behavior of 25cr2ni2mov Steel Welded Joint

Fatigue crack initiation site transition of high‐strength steel under very high‐cycle fatigue

High cycle thermal fatigue of two austenitic stainless steels

Low-cycle fatigue behavior for stainless-clad 304+Q235B bimetallic steel

Low Cycle Fatigue of 9-12% Cr Steel at Elevated Temperature: Cyclic Deformation Behavior and Life Assessment

Experimental Characterization of Competition of Surface and Internal Damage in Very High Cycle Fatigue Regime

Fatigue Life Prediction of A Stainless Steel Plate-Fin Structure Using Equivalent-Homogeneous-Solid Method

Low-cycle Fatigue Behaviour and Fracture Feature of Stainless-Clad Bimetallic Steel

Effect of high temperature on crack initiation of super austenitic stainless steel 654SMO in very high cycle fatigue

Very high‐cycle fatigue behaviour of Ti‐6Al‐4V alloy under corrosive environment

LOW CYCLE FATIGUE FRACTURE FOR 316ti STAINLESS STEEL IN HIGH TEMPERATURE AND PRESSURE WATER

High Cycle Fatigue Of Ti-6al-4v Alloy In Simulated Steam Environment

A fatigue life prediction approach to interior cracking induced high cycle and very high cycle fatigue for surface‐carburized steels