Abstract:The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime Up to 10(7) cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AISI 4340 steel in which the inclusion size is smaller than 5.5 mu m, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 mu m, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 mu m. In the case of internal inclusion-induced fractures at cycles beyond about 1x10(6) for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure N-f in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with N-f, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1x10(6). Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.

Fatigue crack initiation site transition of high‐strength steel under very high‐cycle fatigue

Fatigue hardening/softening behaviour investigated through Vickers microhardness measurement during high-cycle fatigue

Bending Fatigue Behavior of 316L Stainless Steel up to Very High Cycle Fatigue Regime

Microstructure evolution and crack initiation behavior of Q450NQR1 high-strength weathering steel in very high cycle fatigue regime

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

Crack initiation mechanism of titanium alloy in very high cycle fatigue regime at 400°C considering stress ratio effect

Effects of microstructure on crack initiation in super martensitic stainless steel under very‐high‐cycle fatigue at elevated temperature

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Characteristic and mechanism of crack initiation and early growth of an additively manufactured Ti-6Al-4V in very high cycle fatigue regime

Effect of Stress Ratio on Very High Cycle Fatigue Properties of Ti-10V-2Fe-3Al Alloy with Duplex Microstructure

GIGACYCLE FATIGUE OF ULTRA-HIGH STRENGTH STEELS

Influence of microstructure and microdefects on long-term fatigue behavior of a Cr-Mo-V steel

Crack Initiation Mechanism in a High-Strength Ti-5Al-7.5V Alloy Subjected to High Cycle Fatigue Loading

Very high cycle fatigue behavior of a low strength welded joint at moderate temperature

Effects of local microstructure on crack initiation in super martensitic stainless steel under very-high-cycle fatigue

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Fatigue limit evaluation via infrared thermography for a high strength steel with two strength levels

Effect of high temperature on crack initiation of super austenitic stainless steel 654SMO in very high cycle fatigue

Non-inclusion induced crack initiation in multiphase high-strength steel during very high cycle fatigue

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

Mechanism of Fatigue-Life Extension Due to Dynamic Strain Aging in Low-Carbon Steel at High Temperature