Abstract:The influence of hydrogen on defect structure in pure titanium was systemically investigated using X-ray diffraction (XRD) and positron annihilation spectroscopy (PAS). The results showed that hydrogen damage was related to hydrogen concentration, and PAS provided a new idea for the study in the formation of hydride and open volume defects. XRD results showed that two types of titanium hydrides were observed in hydrogen-charged samples, i.e., δ-TiHx and ε-TiH2, and the degree of lattice expansion and the content of hydride increased with hydrogen content. The variation of the S parameter and W parameter indicated that a great deal of vacancy-type defects formed during electrochemical hydrogen charging, and hydrogen atoms could combine with vacancy to form a certain amount of hydrogen-vacancy complexes (HnVm), meanwhile, the hydrogen damage varied significantly with depth. The effective open volume of vacancy-type defect increased with hydrogen charging concentration, and hydrogen-vacancy cluster transformed into HnVm (n < m) cluster, vacancy defects were gradually dominated. In addition, According to the different annihilation environment of positron in titanium hydrides and hydrogen-vacancy complexes, the existence of titanium hydrides and the existing form of hydrogen in defect could be identified in Doppler broadening spectroscopy (CDB). This provided a new way to identify the formation of hydrides and to detect the existing form of low concentration hydrogen in samples.

Effect of hydrogen-vacancy cluster on the tensile strength of alpha-titanium twin boundaries: A first-principles investigation

Diffusion and Retention of Hydrogen in Vanadium in Presence of Ti and Cr: First-principles Investigations

Hydrogen Induced Hardening and Embrittlement of Vanadium Alloys

Effect of helium and vacancies in a vanadium grain boundary by first-principles

Exploration of vacancy defect formation and evolution in low-energy ion implanted pure titanium

First-principles calculation of twin boundary energy and strength/embrittlement in hexagonal close-packed titanium

Atomic scale insights into the fracture behavior along 〈 1 2 - 1 0 〉 and 〈 1 0 1 - 0 〉 oriented twin boundaries in titanium

Improving the Mechanical Processing of Titanium by Hydrogen Doping: A First-Principles Study

Tensile Properties and Fracture Mechanism of the Ti2AlC(0001)/TiAl(111) Interface: Insights from a First-Principles Study

Effect of electrochemical hydrogen charging on defect structure in titanium

Hydrogen interaction with vacancy defects in tungsten: Unraveling the influence on diffusion mechanisms and mechanical properties

The effects of hydrogen and vacancy on the tensile deformation behavior of Σ3 symmetric tilt grain boundaries in pure fe

First-principles analysis of the stability and hydrogen adsorption properties of the α-Ti/α 2 -Ti 3 Al interface towards clarified hydrogen embrittlement mechanism of titanium alloys

Effect of twin boundaries on the strength of body-centered cubic tungsten nanowires

Influence of Titanium on the Clustering of Vacancy, Rhenium and Osmium in Tungsten-Titanium Alloys: First-principles Study

Insights into hydrogen-induced strengthening mechanism of TiC/Ti6Al4V via experiments and first-principles calculations

First-principles insights onto the hydrogen trapping in interstitial-vacancy complexes in vanadium carbide

Hydrogen Diffusion-Induced Crystallographic Changes in Α Plus Β Titanium Alloy

Effect of hydrogen on the basal dissociation of 〈 a 〉-type screw dislocation core in titanium

Hydrogen storage of high entropy alloy NbTiVZr and its effect on mechanical properties: A first-principles study

Role of intracrystalline hydrogen on the ductility of dilute Ti-based alloys by first-principles calculations