Abstract:TiAl alloy is one of the most attractive candidates for a new generation of high-temperature structural materials and has broad application prospects in the aerospace field. As a typical intermetallic material, TiAl is inevitably difficult to process using conventional methods. Election beam selective melting (EBSM) is an effective method of addictive manufacturing to prepare TiAl alloy with a complex structure. However, the microstructure of TiAl alloy formed using EBSM often contains defects such as pores, which seriously reduces the mechanical properties of the material. In this work, the effects of EBSM and post-processing procedures on the microstructure and mechanical properties of Ti-48Al-2Cr-2Nb alloy were studied. The results show that the microstructure of Ti-48Al-2Cr-2Nb alloy formed using the EBSM process was dense and composed of equiaxed γ-phase and double-phase regions. A large number of dislocations that formed due to thermal stress were clearly observed inside the Ti-48Al-2Cr-2Nb alloy. When the EBSM process parameters were 13.5 mA, 4.0 m/s, and 40.50 J/mm3, as the current intensity increased, the Al content decreased, the content of α2 phase increased, and the microstructure of the material was coarse. The results of the tensile test fracture morphology indicate that the Ti-48Al-2Cr-2Nb alloy exhibited brittle fracture during tensile deformation, lacking the typical yield deformation of metal materials. As the energy density of the EBSM process increased, the mechanical properties of the Ti-48Al-2Cr-2Nb alloy first increased and then decreased. The samples prepared with an energy density of 34.50~40.50 J/mm3 had excellent mechanical properties, of which the maximum tensile strength and maximum elongation reached 643 MPa and 2.09%, respectively. The phase composition of the Ti-48Al-2Cr-2Nb alloy after hot isostatic pressing (HIP) treatment remained unchanged from the EBSM samples, but there was a slight difference in content. There was an increase in the amount of γ phase and a decrease in B2 phase, accompanied by the generation of a massive γ phase after HIP treatment. Moreover, the number of dislocations inside the material increased. The Ti-48Al-2Cr-2Nb alloy after HIP treatment exhibited obvious plastic deformation characteristics, with a tensile strength of 679 MPa and elongation of 2.5%. A heat treatment of 900 °C/5 h was performed on the Ti-48Al-2Cr-2Nb alloy after HIP. The dislocation density of the Ti-48Al-2Cr-2Nb alloy decreased, and the B2 phase transformed from massive to lamellar.

Diverse microstructure of Ti6.5Al2Zr1Mo1V fabricated via electron beam selective melting

Hierarchical microstructure of a titanium alloy fabricated by electron beam selective melting

Tuning microstructure and enhancing corrosion property of Ti-6Al-3Nb-2Zr-1Mo alloy through electron beam surface melting

Microstructures Of Ti6a14v Components Synthesized Via Electron Beam Selective Melting

Microstructures Of Components Synthesized Via Electron Beam Selective Melting Using Blended Pre-Alloyed Powders Of Ti6al4v And Ti45al7nb

Performance of Ti6Al4V fabricated by electron beam and laser hybrid preheating and selective melting strategy

TiAl Alloy Fabricated Using Election Beam Selective Melting: Process, Microstructure, and Tensile Performance

Effect of Process Parameters on Microstructure of TiAl Alloy Produced by Electron Beam Selective Melting

Comparison of the microstructures and mechanical properties of Ti–6Al–4V fabricated by selective laser melting and electron beam melting

Research on microstructure of Ti-6Al-4V titanium alloy by thermal simulation under water cooling

Effect of Energy Input on Microstructure and Mechanical Properties in EBSM Ti6Al4V

Metastable phase and microstructural degradation of a TiAl alloy produced via selective electron beam melting

Electron Beam Impact on Microstructure and Microhardness of Ti–6Al–4V Titanium Alloy Produced by Wire Electron-Beam Additive Manufacturing Technology and Selective Laser Alloying at Simulation of Electronic-Beam Welding

Effects of scanning parameters on material deposition during Electron Beam Selective Melting of Ti-6Al-4V powder

Ti-48Al-2Cr-2Nb alloys prepared by electron beam selective melting additive manufacturing: microstructural and tensile properties

An Experimental and Simulation Study on Build Thickness Dependent Microstructure for Electron Beam Melted Ti–6Al–4V

Microstructures and Phases in Electron Beam Additively Manufactured Ti-Al-Mo-Zr-V/CuAl9Mn2 Alloy

Insights into the gradient microstructure and mechanical properties of Ti-6.5Al–2Zr–Mo–V alloy manufactured by electron beam freeform fabrication

The Influence of Electron Beam Welding on the Microstructure of Ti-6Al-4V Alloy Produced by Selective Laser Melting Technology

Microstructure and Mechanical Property of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy Fabricated by Selective Laser Melting with a Preheated Substrate

High-temperature microstructure stability and fracture toughness of TiAl alloy prepared via electron beam smelting and selective electron beam melting