Abstract:Ceramifiable composites based on silicone rubber (SR) filled with mica powder, glass dust (GD) and short glass fiber (SGF) were successfully prepared for high-temperature applications. The effect of the GD/SGF phr ratio in the fluxing agents on the ceramifiable and mechanical properties of the silicone rubber composites was studied. The results demonstrated that the composites showed excellent properties when the ratio of GD/SGF was 1 : 1 and the corresponding tensile strength was 6.5 MPa. The elongation at break of the composites reached 245.4% and the flexural strength of sintered samples produced at 1000 C was 16.2 MPa. Thermogravimetric analysis (TGA) results indicated that the char residue was 57.5% at 700 C, which was much higher than the virgin SR residue. The ceramization process at different sintering temperatures was consequently studied through infrared spectroscopy (IR), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The linear shrinkage and flexural strength of sintered samples increased with increasing sintering temperature from 600 to 1000 C. The FTIR and XRD tests indicated that the fluorophlogopite mica structure was destroyed and a new cristobalite crystalline phase was formed at elevated temperature. The SEM revealed that a coherent and dense microstructure of sintered samples was formed with increased temperatures, which contributed to the flexural strength improvement.

Fabrication and properties of SiO2f/SiO2 composite ceramic based on stereolithography technology

Fabrication by stereolithography of fiber-reinforced fused silica composites with reduced crack and improved mechanical properties

The fabrication of fiber-reinforced polyamine-coated silica paste and the mechanical properties of SiO2/SiO2 composites via stereolithography combined with silica sol impregnation

The Rheological Behaviors and Overcuring Effect of Fiber-Reinforced Polyamine-Coated Silica Paste and the Mechanical Properties of the Composites Via Stereolithography

Fabrication and high-temperature strength of 2.5D SiO2f /SiO2 composites prepared by a combined vacuum impregnation and sol-gel method

Regulation of sintering procedure on property of DLP‐printing SiO2–Al2O3 ceramic: Key of cristobalite precipitation

Effects of volume fraction of short-cut quartz fibers on mechanical and thermal properties of SiO2f/SiO2 composites

Mechanical and dielectric properties of Si3N4/β-SiAlON composite ceramics fabricated by vat photopolymerization 3D printing technology

Mechanical and dielectric properties of porous and wave-transparent Si3N4-Si3N4 composite ceramics fabricated by 3D printing combined with chemical vapor infiltration

Mechanical and Dielectric Properties of Porous Si3n4-Sio2 Composite Ceramics

Microstructure and mechanical properties of continuous carbon fiber-reinforced SiC ceramic composite fabricated by direct ink writing

Curing performance and print accuracy of oxidized SiC ceramic via vat photopolymerization

Effect of the Sintering Temperature on the Microstructure, Properties and Formation Mechanism of Ceramic Materials Obtained from Polysiloxane Elastomer-Based Ceramizable Composites

Effect of Different Forms of Silica on Sintering, Microstructure and Properties of Borosilicate Glass/al2o3 Composites

Fabrication of alumina ceramics with high flexural strength using stereolithography

Silicon carbide ceramics manufactured by digital light processing and low temperature sintering

Microstructures and Mechanical Properties of Pressureless Sintered Ca-3(PO4)(2)/Si3N4 Composite Ceramics

Influence of Sintering Temperature on Microstructure and Mechanical Properties of Al2O3 Ceramic Via 3D Stereolithography

The preparation of ZrO2-Al2O3 composite ceramic by SLA-3D printing and sintering processing

of glass dust and glass fi ber as fl uxing agents for cerami fi able silicone rubber composites

Influence of Hot-Pressing Process on Microstructure and Mechanical Properties of SiO2f/SiO2 Composites