Abstract:Reducing the residual stresses and improving the mechanical strength of large-scale ceramic/metal brazing joints is an important problem that must be solved for its practical engineering application. Using composite filler with solid-state phase transformation ceramic particulates, it is theoretically feasible to relieve the residual stress and improve the mechanical properties of ceramic/metal brazed joints. In this study, Cu mesh, Ag-28Cu-2Ti (wt.%), and YSZ (0.6 mol.% Yttria-stabilized Zirconia solid-state phase transformation ceramic particulates) composite power fillers were used in the brazing of Ti3SiC2 ceramic and pure copper. The microstructure of joints and YSZ particulates in the interface was investigated and confirmed by SEM, EDS, STEM and TEM. In addition, the effect of YSZ particulates content on the mechanical properties of joints was investigated and evaluated by the shear strength. The results show that the interfacial phases were mainly Ti5Si3, TiC, TixCu, Ag (s, s), Cu (s, s) and YSZ particulates. Moreover, most of YSZ particulates undergo the solid-state phase transformation from t-ZrO2 to m-ZrO2 during the cooling process of brazing. The abnormal volume expansion of the solid-state phase transformation reduced the thermal mismatch between Ti3SiC2 ceramic and filler, thereby reducing the residual stress in the interface of joint. When using composite filler with 6wt.% YSZ particulates, the shear strength of Ti3SiC2/Cu joint reached the maximum. The maximum average shear strength of the joints was 80.2 MPa, which was about 103.6% more than the joint without YSZ particulates.This article is protected by copyright. All rights reserved

Brazing of SiO2 ceramic

The brazing of Al2O3 ceramic and other materials

Joining SiO2 based ceramics: recent progress and perspectives

Joints in Si_3N_4 Ceramics Bonded Using Solid-Liquid State Bonding with Intermetallic Compounds Formed in Situ

Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates

Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

A novel high entropy CoFeCrNiCu alloy filler to braze SiC ceramics

Reinforcement of ceramic bonded joints with intermetallic compounds

Recent Advances in Active Metal Brazing of Ceramics and Process

Pressure brazing of Si3N4 ceramics with Al-Li alloy and high temperature properties of the joints

Si3N4 Ceramics Brazing with Composite Soldering Materials

Fabricating porous Si3N4 ceramics joint by ultrasonic brazing at 450 °C

Titanium metallization of Si3N4 ceramics by molten salt reaction: coating microstructure and brazing property

Interfacial Structure and Formation Mechanism of Ultrasonic-Assisted Brazed Joint of Sic Ceramics with Al-12si Filler Metals in Air

Pressure ressure brazing of Si3N4 ceramics with Al-Li alloy and high temperature properties of the joints

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Microstructure and properties of different carbon fiber reinforced ceramic composites brazed joint by Si-Ti alloy filler

Joining of SiC using CoFeCrNiCuTi high entropy alloy filler by electric current field assisted sintering

Solid-Liquid State Bonding of Si3N4 Ceramics with Ceramic-Modified Brazing Alloy

Reaction mechanism and mechanical properties of SiC joint brazed by in-situ formation of Ti3SiC2

Joining of SiC ceramics using the Ni-Mo filler alloy for heat exchanger applications