Abstract:The crystallization process of β zeolite has been investigated by using FT-IR, XRD, TG, SEM, and ICP-AES. The samples were obtained by hydrothermal synthesis at 140 °C and chemical composition of the mixture used for synthesis can be expressed as n(Al2O3) : n(SiO2) : n(TEABr) : n (Na2O) : n(NaF) : n(H2O) : n [(NH4)2O] = 1 : 25 : 7. 5 : 2. 5 : 3. 75 : 550 : 6. 25. The crystallization curve of zeolite β exhibits a typical S-shaped characteristic. The typical framework IR-absorptions at 567 and 518 cm-1 have different natures. The former is detected at the beginning of induction period and its intensity changes a little in induction period, but exhibits a direct correlation with crystallinity in growth period. The latter is not detected in the induction period, but exhibits the same trend in growth period. The large amorphous SiO2-Al2O3 particles which are visible at the beginning of crystallization change into small grains during the induction period. n(SiO2)/n(Al2O3) ratio of the solid phases obtained at different synthesis time changes significantly during the induction period, but changes a little in growth period. So the β zeolite crystal nucleus are formed via liquid-phase synthesis mechanism. A typical gel in synthesis of β zeolite is transformed initially into a solid, which contains richer aluminium, minor F- and occluded TEA species. The aluminosilicate gel particles are dissolved by F- during the induction period and the transition complex, which has a specific weak X-ray diffraction peak at 2θ = 22. 8° and specific DTG pattern, is formed at the turning point from induction period to growth period. During the growth period Si and Al transport from the liquid to the solid phase at almost the same rates. F- anion has greater influence on the formation and turning of transition complex.

Investigation of a Liquid-Mediated Defect-Healing Treatment in Zeolite Beta

Improving mechanical stability of ZSM-5 zeolite by defect-healing treatment

Extremely Stable Zeolites Developed via Designed Liquid-Mediated Treatment

A high‐resolution solid‐state NMR study on nano‐structured HZSM‐5 zeolite

Effect of HF Treatment on Structure and Acidity of Β Zeolite

Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy

Synthesis of β Zeolite Using Tetraethylammonium Bromide Together with Fluoride as Composite of Template (II) - Studies on Crystallization Process of β Zeolite

Effects of residual alkali metals on the hydrothermal/thermal stability of silicalite-1

Generation of Parallelepiped-Shaped Mesopores and Structure Transformation in Highly Stable Ferrierite Zeolite Crystals by Framework Desilication in NaOH Solution

Effect of defect-healing treatment on layered silicate precursors toward well-defined crosslinked frameworks

Studies on THF-FER zeolite: I. Stability of crystal structure

Al distribution and structural stability of H-BEA zeolites at different Si/Al ratios and temperatures: a first-principles study

Molecular Simulation of the Impact of Defects on Electrolyte Intrusion in Zeolites

Incorporation of Al3+ Ions to Promote the Stabilization Effect of (nh4)(2)sif6 Treatment on the Hydrothermal Stability of Mesoporous Sba-15 Zeolite

Tracking the Chemical Transformations at the Brønsted Acid Site Upon Water-Induced Deprotonation in a Zeolite Pore

Effect of dealumination defects on the properties of zeolite Y

Unravelling the Crucial of Spatial Al Distribution to Realize Precise Alkali‐Treatment for Target Acid‐Catalyzed Reactions

Removing Fluoride from Double Four-Membered Rings Yielding Defect-Free Zeolites under Mild Conditions Using Ozone

Synthesis and characterization of β zeolite from aluminosilicate sol containing fluorion

Synthetic Control of the Defect Structure and Hierarchical Extra-Large-/Small-Pore Microporosity in Aluminosilicate Zeolite SWY

From Layered Zeolite Precursors to Zeolites with a Three-Dimensional Porosity: Textural and Structural Modifications Through Alkaline Treatment