Abstract:Introduction of mesopore is critical for applications where mass-transport limitations within microporous networks, especially for zeolite with one-dimensional microporous network, hinder their performance. Generally, the creation of mesopore in zeolite through a direct synthesis route is strongly dependent on complex and expensive organic molecules, which limits their commercial application. Here, we successfully developed a facile synthesis route for preparing ZSM-48 zeolite (*MRE topology) with ultralarge mesoporosity in which typical 1,6-hexylenediamine worked as an organic structure-directing agent, innovatively assisted by a simple crystal growth modifier (tetraethylammonium bromide, TEABr). The working mechanism of TEABr during crystallization was revealed and proposed on the basis of TEM, thermal gravimetric mass spectrum, and 13C cross-polarization magic angle spinning NMR characterization results. In the process, TEA+ ions preferentially interacted with the solid during the induction period, which effectively suppressed the aggregation of ZSM-48 primary nanorods. As a result, ultralarge mesoporosity of 0.97 cm3·g–1 was constructed through the stacking of the nanorods. Interestingly, TEA+ ions only took part in the crystallization process and did not occlude in the pores of the final zeolites indicating its potential in recyclability. Moreover, similar synthesis strategy could be applied for the preparation of hierarchical ferrierite zeolites, implying the universality of this strategy. Compared with a conventional sample, ZSM-48 zeolite with ultralarge mesoporosity showed superior catalytic stability in the m-xylene isomerization reaction due to its significantly enhanced diffusion and mass transfer capability, which will greatly promote the practical application of ZSM-48 zeolite.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c09137?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c09137</a>.Ferrierite zeolite synthesis; SEM images; 13C CP/MAS NMR spectra; MX conversion and PX selectivity; NH3-TPD profiles; adsorption isotherms of MX; TG results; and textural properties of samples before and after reaction (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c09137/suppl_file/am1c09137_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Generation of Parallelepiped-Shaped Mesopores and Structure Transformation in Highly Stable Ferrierite Zeolite Crystals by Framework Desilication in NaOH Solution

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Insights into the topotactic conversion process from layered silicate RUB-36 to FER-type zeolite by layer reassembly

From Layered Zeolite Precursors to Zeolites with a Three-Dimensional Porosity: Textural and Structural Modifications Through Alkaline Treatment

Exfoliated Ferrierite-Related Unilamellar Nanosheets in Solution and Their Use for Preparation of Mixed Zeolite Hierarchical Structures

Direct Preparation of *MRE Zeolites with Ultralarge Mesoporosity: Strategy and Working Mechanism

Studies on Crystallography, Stability, Acidity and Skeletal Isomerization of C5 Olefins of THF–FER Zeolite

FER zeolite crystallized in THF–Na2O–SiO2–Al2O3–H2O reactant system containing catalytic amount of organic additives

Studies on THF-FER zeolite: I. Stability of crystal structure

High-silica FER zeolite synthesized in tetrahydrofuran/water systems with VPT method

Synthesis of FER Zeolite Using 4-(Aminomethyl)pyridine as Structure-directing Agent

HIGH-SILICA FER ZEOLITE SYNTHESIZED IN THF/H2O SYSTEMS BY VPT METHOD

Study on the Formation of Mesopore During Hydrothermal Dealumination of Y Zeolite

Synthesis of Millimeter-Sized Spherical Ferrierite Zeolite by Vapor-Assisted Conversion

Single-Step Delamination of A Mww Borosilicate Layered Zeolite Precursor under Mild Conditions Without Surfactant and Sonication

Templating of high-silica zeolites by tetrahydrofuran in the Na2O – SiO2 – Al2O3 – H2O system

Solvent Evaporation Assisted Preparation of Oriented Nanocrystalline Mesoporous MFI Zeolites

Mesoscale Reorganization of the Depolymerized Aluminosilicate into Single-Crystalline Hierarchical Zeolite

Facile Morphology and Porosity Regulation of Zeolite ZSM-5 Mesocrystals with Synergistically Enhanced Catalytic Activity and Shape Selectivity

Crystal Engineering of Hierarchical Zeolite in Dynamically Maintained Pickering Emulsion

Extremely Stable Zeolites Developed via Designed Liquid-Mediated Treatment