Abstract:Using single metal salts of zirconium, lanthanum, and iron as raw materials and sodium alginate as a cross-linking agent, a new composite adsorbent was prepared via the co-precipitation method and embedding immobilization technology, and its phosphorus adsorption performance in wastewater was evaluated. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) were used for characterization, and a 0.5 mol·L−1 sodium hydroxide solution was used to regenerate the adsorbent. The experimental results demonstrated that the adsorption rate reached 99.88% when the wastewater volume was 50 mL, the initial concentration of phosphorus-containing wastewater was 5 mg·L−1, the pH was 5, the dosage of composite adsorbent was 0.2 g, and the adsorption time was 200 min. The prepared adsorbent could reduce the initial phosphorus concentration of 5 mg·L−1 to 0.006 mg·L−1 in simulated wastewater, and from 4.17 mg·L−1 in urban sewage to undetected (<0.01 mg·L−1), thus meeting the discharge requirements of the grade A standard of the Urban Sewage Treatment Plant Pollutant Discharge Standard (GB18918-2002). The adsorption process conformed to the Freundlich adsorption isothermal equation and quasi-second-order kinetic equation, and the adsorption reaction was exothermic and spontaneous. More importantly, after three lye regeneration tests, the removal rate of phosphorus in water remained above 68%, that is, the composite adsorbent could be reproducibly fabricated and recycled. The characterization results showed that the surface of the composite adsorbent was rough, with a complex pore structure. After phosphorus removal, the surface morphology of the composite adsorbent showed a similar honeycomb structure, with a P-H, P-O stretching vibration peak and a characteristic P2p peak. At the same time, the proportion of hydroxyl groups (M-OH) on the metal surface decreased after adsorption. Our findings thus demonstrate that the mechanism of phosphorus removal is mainly based on the coordination exchange reaction between phosphate and metal active sites and surface hydroxyl groups, resulting in the formation of granular phosphate deposits.

Preparation of Fe(III) Peeling‐Intercalation Ball Clay/Oyster Shell Composites and Phosphorus Removal from Wastewater

Alkali-Treated Yttrium-Containing Chitosan-Based Hydrogel Beads for Phosphate Removal from Aqueous Solutions

Preparation and Phosphorus Removal Performance of Zr–La–Fe Ternary Composite Adsorbent Embedded with Sodium Alginate

Preparation, Optimization, and Application of Sustainable Ceramsite Substrate from Coal Fly Ash/waterworks Sludge/oyster Shell for Phosphorus Immobilization in Constructed Wetlands

Adsorption Performance and Its Mechanism of Aqueous As(III) on Polyporous Calcined Oyster Shell-Supported Fe-Mn Binary Oxide.

Removal of phosphate from aqueous solution by ferrihydrite/bagasse composite prepared through in situ precipitation method

Preparation and Characterization of Ferric-Impregnated Granular Ceramics (fgcs) for Phosphorus Removal from Aqueous Solution

Equilibrium and Kinetics Studies of Phosphate Removal from Solution Onto a Hydrothermally Modified Al-Si-Fe-Ca Composite Adsorbent

Removal Mechanisms of Phosphate from Water by Calcium Silicate Hydrate Supported on Hydrochar Derived from Microwave-Assisted Hydrothermal Treatment

Removal of phosphorus from water bodies using high-performance ceramsite prepared from solid wastes

Performance and adsorption mechanism of a magnetic calcium silicate hydrate composite for phosphate removal and recovery

Removal of Phosphate Solution Using Bio-Sorbent Prepared by Agricultural Byproduct

Iron-loaded magnetic alginate-chitosan double-gel interpenetrated porous beads for phosphate removal from water: Preparation, adsorption behavior and pH stability

Removal of Phosphorus Using Biochar Derived from Fenton Sludge: Mechanism and Performance Insights.

Preparation and practical applications of a phosphate capture material with FeO(OH)-loaded polyurethane

Phosphate Removal Mechanisms in Aqueous Solutions by Three Different Fe-Modified Biochars

β-FeOOH Modified Sludge Biochar as Efficient Adsorbent for Phosphate Removal

In situ formation of Ca(OH)2 coating shell to extend the longevity of zero-valent iron biochar composite derived from Fe-rich sludge for aqueous phosphorus removal

Preparation of FeOOH Supported by Melamine Sponge and Its Application for Efficient Phosphate Removal

Preparation of Fe/Zr bimetallic oxide beads and its performance and mechanism for advanced treatment of actual phosphorus-containing wastewater

Effectiveness and Mechanisms of Phosphate Adsorption on Iron-Modified Biochars Derived from Waste Activated Sludge