Abstract:Kaolinite-urea intercalation complex was prepared using kaolinite as intercalation host and urea as intercalating agent. The kaolinite-urea intercalation complex was used as precursor to prepare exfoliated kaolinite by deintercalating urea molecules from the interlayers of kaolinite through ultrasonic treatment. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize the as-prepared exfoliated kaolinite. A broad 001 diffraction of kaolinite with weak intensity showed the random orientation of kaolinite platelets. SEM micrograph confirmed the exfoliation of kaolinite particles with layer thickness of no more than 50 nm. The exfoliated kaolinite particles were used as filler to poly(ethylene-oxide)/LiClO4 (PEO/LiClO4) system to prepare PEO/kaolinite composites, with the aim to improve the ion conductivity and mechanical property of the PEO matrix. SEM, transmission electron microscopy (TEM), XRD and Fourier transform infrared spectroscopy (FTIR) were used to characterize the PEO/kaolinite composites. SEM and TEM micrographs exhibited a good dispersion of exfoliated kaolinite in PEO matrix. XRD results showed that the crystallinity of PEO was gradually decreasing with increased exfoliated kaolinite content. FTIR analysis indicated that the hydrogen bonding was formed between the oxygen atoms of PEO segments and the hydroxyl groups on kaolinite surface, and this interaction between PEO and kaolinite was beneficial to the decrease in crystallinity of PEO. In order to evaluate the effect of the exfoliated kaolinite on ion conductivity and mechanical property of PEO matrix, AC impedance measurement and mechanical test were carried out. The results indicated that the ion conductivity of the composites gradually increased with increased exfoliated kaolinite content and reached 6.0 x 10(-5) S/cm at filler concentration of 20 wt%. The formation of amorphous region around the exfoliated kaolinite was beneficial for the Li+ ion conduction in PEO matrix. When the exfoliated kaolinite content reached 10 wt%, the formed amorphous regions were connected to each other to form a network for the transport of Li+ in the interconnected amorphous regions, leading to a sharp increase in ion conductivity. Moreover, the prepared composites under different drying temperature exhibited different ion conductivity. The reason was attributed to the change of PEO crystallinity with drying temperature, and the change trend of the ion conductivity was consistent with that of PEO crystallinity. Under the drying temperature of 95 degrees C, the as-prepared composite possessed high ion conductivity (6.8 x 10(-5) S/cm). In addition, the Young's modulus and tensile strength of the composites were improved because of the introduction of the exfoliated kaolinite into EPO matrix. The composites showed the maximal increase of 256% and 121% in Young's modulus and tensile strength, i.e., to 165.1 MPa and 6.743 MPa respectively, compared to PEO/LiClO4 (46.3 and 3.047 MPa). Therefore, the exfoliated kaolinite was a promising filler to prepare PEO based polymer electrolyte.

Collaborative improvement of electrical‐thermal‐mechanical properties of kaolin‐filled ethylene propylene diene monomer and mechanism analysis

Investigation of mechanical and wear properties of kaolin filled UHMWPE composites

Preparation and Properties of Damping Materials in Multi-Phase System

Study on the erosion wear characteristics and mechanisms of UBHMWPE/kaolin composites

Enhanced Sound Insulation and Mechanical Properties Based on Inorganic Fillers/thermoplastic Elastomer Composites

Tribological properties of kaolin filled UHMWPE composites in unlubricated sliding

Preparation and Characterization of Poly(ethylene-oxide)/Kaolinite Composite Electrolyte

The Role of Exfoliated Kaolinite on Crystallinity, Ion Conductivity, Thermal and Mechanical Properties of Poly(ethylene Oxide)/kaolinite Composites

Photoinitiated Crosslinking of EPDM/inorganic Filler Blends and Characterization of Related Properties

Preparation of nanoalumina/EPDM composites with good performance in thermal conductivity and mechanical properties

Preparation and Characterization of Composites: Ethylene–propylene–diene Terpolymer‐graft‐maleic Anhydride/caco3

Effect of lignin on the structure-property behavior of metal-coordinated and chemically crosslinked ethylene-propylene-diene-monomer composites

Preparation and Characterization of Composites: Epdm-G-Aa/Caco3

Preparation and study on electrical/thermal properties of epoxy/polyacrylate rubber composite dielectric

Novel Preparation and Properties of EPDM/montmorillonite Nanocomposites

Ameliorated DC Insulation Performance of EPDM through Chemical Grafting with a Voltage Stabilizer

Improved Body and Interface Properties of EPDM Insulation for HVDC Cable Accessory by Grafted Voltage Stabilizer

Low Dielectric Loss and Infrared Emissivity Coating with Enhanced Mechanical Property by Grafting Modification of EPDM

Significantly Improved Electrical Properties of Photo-Initiated Auxiliary Crosslinking EPDM Used for Cable Termination

Breaking graphite through a ball-milling process: the thermal conductivity and mechanical properties of polyethylene composites

Preparation and Mechanical Properties Analysis of Rare Earth Filling Ethylene‐Allene Monomer Rubber Composite