Abstract:In this paper, the unilateral tension of α-Fe in the local region of the crack tip are simulated by molecular dynamics method, the plastic deformation behaviors and hydrogen embrittlement mechanism of the crack tip under different hydrogen concentration and hydrogen positions are analyzed. The results show that for the hydrogen-containing models, there exists a critical hydrogen concentration c 0 that can make the plasticity of the α-Fe material reduce greatly. For the crack-free model, the main hydrogen embrittlement mechanism is adsorption-induced dislocation emission (AIDE), and the critical hydrogen concentration c 0 is 0.3 %. When the hydrogen concentration c H < c 0 , the plastic deformation mechanism is mainly dominated by phase transformation; when c H ≥ c 0 , the plastic deformation mechanism is phase transformation at low strains and dislocation motion at high strains. For the cracked model, the main mechanism of hydrogen embrittlement is hydrogen-enhanced local plasticity at the crack tip, with a critical c 0 of 1.7 %. When c H < c 0 , the plastic deformation mechanism of the model is a combination of phase transformation and dislocation; when c H ≥ c 0 , the plastic deformation mechanism is controlled by phase transformation. When the hydrogen is far away from the crack tip, the local mechanical behavior of the crack tip does not change significantly, while when hydrogen gathered at the crack tip, the addition of a small amount of hydrogen atoms will make the fracture strain decrease rapidly, which shows a mechanism of hydrogen-enhanced strain-induced vacancies (HESIV). A saturation value of hydrogen concentration at the crack tip is confirmed in this paper, when the local hydrogen concentration exceeds this saturation value, the plastic behaviour tends to be stable. The influence of hydrogen atoms distribution on the crack initiation behavior was determined by atomic configuration analysis.

Elastic-plastic crack-tip field in hydride forming metals under hydrogen chemical equilibrium

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Hydrogen diffusion behavior within microstructures near crack tip: A crystal plasticity study

Strain gradient plasticity-based modeling of hydrogen environment assisted cracking

Unveiling Remarkable Hydrogen Accumulation Near Ferrite Crack Tip: Role of Unloading Effect

Molecular dynamics study on the effect of hydrogen on the plastic behavior of α-Fe crack tip

Strain gradient plasticity modeling of hydrogen diffusion to the crack tip

A phase field model for elastic-gradient-plastic solids undergoing hydrogen embrittlement

Tailoring negative pressure by crystal defects: Crack induced hydride formation in Al alloys

Effect of Hydrogen on Plastic Deformation Near Crack-tip of A537 Steel in 3.5%nacl Solution

Special Fatigue Fracture Behavior of Nanocrystalline Metals under Hydrogen Conditions

A phase field formulation for hydrogen assisted cracking

Hydride-enhanced strain localization in zirconium alloy: a study by crystal plasticity finite element method

Computational modelling of hydrogen assisted fracture in polycrystalline materials

Effect of hydrogen embrittlement on dislocation emission from a semi-elliptical surface crack tip in nanometallic materials

Computational predictions of hydrogen-assisted fatigue crack growth

Special Fracture Behavior of Nanocrystalline Metals Driven by Hydrogen

On the effects of transformation strain induced by hydride precipitation

Effect of pre-strain on critical conditions for hydrogen-induced delayed cracking and crack nucleation characteristic of DP1180 steel

A Theoretical Model for Delayed Hydride Cracking Velocity Considering the Temperature History and Temperature Gradients

A Phase-Field Regularized Cohesion Model for Hydrogen-Assisted Cracking