Optimization of preparation conditions and performance of a new degradable soil water retaining agent

Zhang Yumang,Wang Yongheng,Wang Chengyu,Gao Yunhang,Liu Shuxia,Xie Zhonglei,Chang Hongyan

DOI: https://doi.org/10.1038/s41598-024-60784-2

IF: 4.6

2024-05-20

Scientific Reports

Abstract:Using polyaspartic acid (PAsp) and bentonite (BT) as the main raw materials, a new type of degradable soil water retaining agent (PAsp-AA/BT) was synthesized by microwave radiation. The optimum synthesis conditions and comprehensive properties of PAsp-AA/BT were discussed and the structure and surface characteristics of PAspsp-AA/BT were characterized by FTIR, SEM, XRD and TGA in the paper. The results showed that the optimum synthesis conditions of PAsp-AA/BT were as follows: the dosages of polyaspartic acid (PAsp), bentonite (BT), initiator potassium persulfate, crosslinking agent N , N ′-methylene bisacrylamide was 5, 3, 0.3, 0.03%, respectively, the neutralization degree of acrylic acid was 75%, and the microwave power was 490W. Under this condition, the absorption ratio of the synthesized PAspsp-AA/BT in deionized water and 0.9% NaCl solution was 953 and 164 g/g, respectively. The synthesized PAsp-AA/BT had a high water absorption rate, good water retention and repeated water absorption, and the degradation rate in soil within 30 days reached 32.75%, with good degradation effect. The analysis of SEM, FT-IR, XRD and TGA showed that: the surface of PAsp-AA/BT was rough and had obvious pore structure, which was conducive to the diffusion of water molecules; polyaspartic acid, bentonite and acrylic acid were polymerized; the cross-linking structure was formed between polyaspartic acid, bentonite and acrylic acid; the product of PASP-AA/BT had good thermal stability. This study provides a new soil water retaining agent, which is helpful for the better development of soil water retaining agent research.

multidisciplinary sciences

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop a new type of degradable soil water - retaining agent in response to the frequent droughts and water shortages caused by global climate change. Specifically, the researchers used polyaspartic acid (PAsp) and bentonite (BT) as the main raw materials and synthesized a new degradable soil water - retaining agent (PAsp - AA/BT) through microwave irradiation. The main purposes of the paper are:

1. **Optimize synthesis conditions**: Through single - factor variable tests, the effects of different amounts of raw materials, amounts of cross - linking agents and initiators, degree of neutralization, microwave power and time on the liquid absorption rate of the water - retaining agent were explored, and the optimal synthesis conditions were determined.
2. **Evaluate performance**: The degradable soil water - retaining agent prepared under the optimal synthesis conditions was discussed in terms of its liquid absorption rate, water retention rate, degradation rate and repeated water absorption performance.
3. **Structural characterization**: The structure of the degradable soil water - retaining agent was characterized by Fourier transform infrared spectroscopy (FT - IR), scanning electron microscopy (SEM), X - ray diffraction (XRD) and thermogravimetric analysis (TGA).

The research results show that under the optimal conditions, the synthesized PAsp - AA/BT has liquid absorption ratios of 953 g/g and 164 g/g in deionized water and 0.9% NaCl solution respectively. This water - retaining agent has a high water absorption rate, good water - retaining performance and repeated water - absorption ability, and the degradation rate in the soil within 30 days reaches 32.75%, showing a good degradation effect. These results provide new methods and materials for land desertification control, drought - resistance and water - saving in agriculture and forestry.