Abstract:ZSM-5 zeolite is a kind of high-value-added porous aluminosilicate zeolite. The use of the coal gasification slag utilization process by-product desilication liquid as a silicon raw material to replace the current raw materials such as water glass will help reduce production costs and achieve high-value utilization of solid waste. ZSM-5 zeolites for volatile organic compounds (VOCs) adsorption were prepared by a one-step hydrothermal method using the desilication solution prepared from coal gasification slag as the main silicon source and sodium source. The effects of crystallization reaction time, the crystallization temperature, the Na2O/SiO2 molar ratio, and the SiO2/Al2O3 molar ratio on the relative crystallinity and the specific surface area of the ZSM-5 zeolite were investigated and optimized. The optical reaction conditions were as follows: a crystallization time of 12 h, a crystallization temperature of 170 °C, a Na2O/SiO2 molar ratio of 0.2, and a SiO2/Al2O3 molar ratio of 200. The optimal ZSM-5 zeolite synthesized is hexagonal, with regular grains, a relative crystallinity of 101.48%, a specific surface area of 337.48 m2·g−1, and a pore volume of 0.190 cm3·g−1. And the optimal ZSM-5 zeolite was composed of SiO2 content of 97.52 wt%, Al2O3 content of 1.58 wt%, Na2O content of 0.33 wt%, and SiO2/Al2O3 molar ratio of 104.93. Na2O/SiO2 molar ratio is 0.0033. The results of static adsorption experiments show that the static adsorption capacities of ZSM-5 zeolite for p-xylene, benzene, toluene, and butyl acetate were 118.85, 69.98, 68.74, and 95.85 mg·g−1, respectively, which can effectively adsorb VOCs. The synthetic process of the ZSM-5 zeolite is a simple preparation process and short in synthesis time. The results of this study not only help to realize the high-value utilization of silicon components in solid waste, but also provide an economical and effective way to synthesize VOCs adsorption materials.

What problem does this paper attempt to address?

The main problem this paper attempts to address is the preparation of ZSM-5 molecular sieve using desilicated coal slag solution as the primary silicon and sodium source through hydrothermal synthesis, for the adsorption of volatile organic compounds (VOCs). Specifically, the study aims to: 1. **Reduce production costs**: By using desilicated coal slag solution to replace traditional raw materials (such as water glass), production costs can be reduced. 2. **Achieve high-value utilization of solid waste**: Transform the solid waste coal slag produced during the coal gasification process into valuable ZSM-5 molecular sieve, achieving efficient resource utilization. 3. **Optimize synthesis conditions**: Investigate the effects of crystallization reaction time, crystallization temperature, Na₂O/SiO₂ molar ratio, and SiO₂/Al₂O₃ molar ratio on the relative crystallinity and specific surface area of ZSM-5 molecular sieve, and optimize these conditions. 4. **Improve adsorption performance**: The prepared ZSM-5 molecular sieve has a high specific surface area and good pore structure, which can effectively adsorb VOCs. Through these studies, the authors hope to develop a simple, fast, and green method for synthesizing ZSM-5 molecular sieve, which not only helps achieve high-value utilization of solid waste but also provides an economical and effective way to prepare VOCs adsorption materials.

A Hydrothermal Synthesis Process of ZSM-5 Zeolite for VOCs Adsorption Using Desilication Solution

Effect of Hydrothermal Treatment on Suppressing Coking of Zsm-5 Zeolite During Methanol-To-Propylene Reaction

Hydrothermal synthesis of high crystallinity ZSM-5 zeolite from coal gasification coarse slag and mother liquor circulation for efficient coal chemical wastewater purification

Synthesis of Zsm-5 Aggregates Made of Zeolite Nanocrystals Through A Simple Solvent-Free Method

Facile synthesis of mesoporous ZSM-5 aided by sonication and its application for VOCs capture

Synthesis of High-silica ZSM-5 Zeolite by Vapor-phase Transport Method

One-step Synthesis of Zeolite ZSM-5 from Perlite Tailings by Crystal Seed Solution Assisted Method

Solid Phase ZSM-5 Synthesis from Coal Gasification Coarse Slag

Facile and controllable preparation of nanocrystalline ZSM-5 and Ag/ZSM-5 zeolite with enhanced performance of adsorptive desulfurization from fuel

Preparation and characterization of ZSM-5 molecular sieve using coal gangue as a raw material via solvent-free method: Adsorption performance tests for heavy metal ions and methylene blue

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

Role of silicon in the growth of ZSM-5 synthesized with coal fly ash as raw materials

Enhanced hydrophobic ZSM-5 with high capacity for toluene capture under high-humidity conditions

Preparation of Zeolite X by the Aluminum Residue From Coal Fly Ash for the Adsorption of Volatile Organic Compounds

In-Situ Synthesis of Zsm-5 Zeolite from Metakaolin/Spinel and Its Catalytic Performance on Methanol Conversion

Synthesis of ZSM‐5 zeolite from fly ash by one‐pot hydrothermal method for methylene blue removal

Solvent-free and Mesoporogen-free Synthesis of Mesoporous Aluminosilicate ZSM-5 Zeolites with Superior Catalytic Properties in the Methanol-to-Olefins Reaction

Optimization of crystal growth of hierarchical porosity ZSM-5 zeolite based on coal fly ash "waste utilization"Optimierung des Kristallwachstums hierarchischer Porositat ZSM-5-Zeolith auf Basis von Kohlenflugasche Mull-Verwendung"

Synthesis of ZSM-5 zeolites using palygorskite as raw material under solvent-free conditions

Preparation of a High-Silicon ZSM-5 Molecular Sieve Using Only Coal Gangue as the Silicon and Aluminum Sources

Controlled design of Na-P1 zeolite/ porous carbon composites from coal gasification fine slag for high-performance adsorbent