Abstract:ZSM-5 zeolite is a kind of high-value-added porous aluminosilicate zeolite. The use of the coal gasification slag utilization process by-product desilication liquid as a silicon raw material to replace the current raw materials such as water glass will help reduce production costs and achieve high-value utilization of solid waste. ZSM-5 zeolites for volatile organic compounds (VOCs) adsorption were prepared by a one-step hydrothermal method using the desilication solution prepared from coal gasification slag as the main silicon source and sodium source. The effects of crystallization reaction time, the crystallization temperature, the Na2O/SiO2 molar ratio, and the SiO2/Al2O3 molar ratio on the relative crystallinity and the specific surface area of the ZSM-5 zeolite were investigated and optimized. The optical reaction conditions were as follows: a crystallization time of 12 h, a crystallization temperature of 170 °C, a Na2O/SiO2 molar ratio of 0.2, and a SiO2/Al2O3 molar ratio of 200. The optimal ZSM-5 zeolite synthesized is hexagonal, with regular grains, a relative crystallinity of 101.48%, a specific surface area of 337.48 m2·g−1, and a pore volume of 0.190 cm3·g−1. And the optimal ZSM-5 zeolite was composed of SiO2 content of 97.52 wt%, Al2O3 content of 1.58 wt%, Na2O content of 0.33 wt%, and SiO2/Al2O3 molar ratio of 104.93. Na2O/SiO2 molar ratio is 0.0033. The results of static adsorption experiments show that the static adsorption capacities of ZSM-5 zeolite for p-xylene, benzene, toluene, and butyl acetate were 118.85, 69.98, 68.74, and 95.85 mg·g−1, respectively, which can effectively adsorb VOCs. The synthetic process of the ZSM-5 zeolite is a simple preparation process and short in synthesis time. The results of this study not only help to realize the high-value utilization of silicon components in solid waste, but also provide an economical and effective way to synthesize VOCs adsorption materials.

Synthesis of High-silica ZSM-5 Zeolite by Vapor-phase Transport Method

Fast Synthesis of High-Silica Zsm-5 Zeolite Via A Simple Vapor-Phase Transport Method

A Novel Method for the Preparation of Zeolite ZSM-5

One-step Synthesis of Zeolite ZSM-5 from Perlite Tailings by Crystal Seed Solution Assisted Method

A Hydrothermal Synthesis Process of ZSM-5 Zeolite for VOCs Adsorption Using Desilication Solution

Crystallization Behavior of ZSM-35 Zeolite in Seed-Assisted VPT Synthesis System

Synthesis zeolites in water vapour phase and their properties

Facile synthesis of mesoporous ZSM-5 aided by sonication and its application for VOCs capture

Crystallization Process of Zeolite ZSM-5 and Zeolite ZSM-35 in a Special Autoclave

Synthesis of Zsm-5 Aggregates Made of Zeolite Nanocrystals Through A Simple Solvent-Free Method

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Directly synthesis of H-form ZSM-5 zeolites with n-butylamine in the presence of seed and ethanol

Synthesis of nano-ZSM-5 zeolite via a dry gel conversion crystallization process and its application in MTO reaction

Zeolitization of diatomite to prepare hierarchical porous zeolite materials through a vapor-phase transport process

Synthesis of ZSM-5 Zeolite Using Γ-Aminopropyl Triethoxylsilane As Structure-directing Agents

Optimization of crystal growth of sub-micron ZSM-5 zeolite prepared by using Al(OH)3 extracted from fly ash as an aluminum source

SYNTHESIS OF ZSM-5 ZEOLITE MEMBRANE ON DIFFERENT CARRIERS BY ONE STEP IN SITU HYDROTHERMAL METHOD

Preparation of ZSM-5 molecular sieve by diatomaceous earth in-situ crystallization

Direct Synthesis of Zeolites from a Natural Clay, Attapulgite

High-silica FER zeolite synthesized in tetrahydrofuran/water systems with VPT method

Synthesis of Pure-silica BETA Zeolite by the Method of Seed-direct Steam-assisted Crystallization