Abstract:In this work, the effects caused by both the amount of air-entraining agent (AEA) and freeze-thaw cycles on microstructure of high-strength concrete have been analyzed. For this purpose, five series of concrete specimens have been manufactured, each of them containing a different amount of AEA. Then, all series have been subjected to up to 300 freeze-thaw cycles. In addition, the specimens have been analyzed using a computed tomography (CT) scan device at pre-defined freeze-thaw cycles and all data have been processed with digital image processing (DIP) software.The results reveal, on the one hand, that the quantity of AEA has a greater influence on pore structure, and additionally the freeze-thaw action only slightly modifies the pore structure. As AEA increases, a progressive rise of the porosity and the number of pores is observed up to a maximum value. Next, a decrease is noticed. Moreover, there is not a linear relation between porosity and AEA. Furthermore, as AEA increases, a variation of its size and shape is observed. Alternatively, the effect of freeze-thaw cycles is more complex and does not show a monotonous tendency. The results reveal that the first 50 freeze-thaw cycles have the strongest influence on pore structure, observing a decrease in porosity. For the rest of the cycles, the porosity increases progressively resulting, after 300 freeze-thaw cycles, in a slightly lower porosity in almost all series than in those presented at the beginning. Hydration of unhydrated cement particles alongside with microcracking act as opposite performances during the freeze-thaw cycles. Therefore, this can suggest that, under these conditions, freeze-thaw action is not able to damage significantly the microstructure of concrete.The results show that the series with a lower AEA content show a better behavior under freeze-thaw cycles. In this case, the specimens exhibit a lower porosity and a higher level of small pores, and the pores evince a more elongated shape. All these features lead to a more impermeable concrete and, therefore, with a better performance under freeze-thaw cycles.

Pore structure, mechanical property and permeability of concrete under sulfate attack exposed to freeze–thaw cycles

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Effect of freeze–thaw cycles on the stress–strain curves of unconfined and confined concrete

Influence of air-entraining agent and freeze-thaw action on pore structure in high-strength concrete by using CT-Scan technology

Degradation Mechanism and Numerical Simulation of Pervious Concrete under Salt Freezing-Thawing Cycle

Degradation of mechanical properties of concrete caused by freeze-thaw action

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

Microstructural Damage Characterization Of Concrete Under Freeze-Thaw Action

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Deterioration of concrete under the coupling action of freeze–thaw cycles and salt solution erosion

Stress-strain relationship of concrete in freeze-thaw environment

Quantifying Effect of Later Curing on Pores of Paste Subject to Early-Age Freeze-Thaw Cycles by Different Techniques

Mechanical characteristics and freezing-thawing degradation mechanism for mortar samples under sodium sulfate solutions attack

Effect of Saturation Degree on Concrete Deterioration Due to Freeze-Thaw Action

Study on pore structure and the mechanical properties of sandstone-concrete binary under freeze-thaw environment

Three-Dimensional Mesonumerical Model of Freeze-Thaw Concrete Based on the Porosity Swelling Theory

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle

Effect of dry–wet ratio on pore-structure characteristics of fly ash concrete under sulfate attack