Abstract:The previous researches mainly focused on the freeze-thaw damage of fully saturated rocks. However, most of the nature rocks experience incomplete water saturation and it may not reach the threshold of frost cracking of a void, at least 91% water saturation considering the 9% volumetric expansion of freezing water and ignoring water flow. A serious freeze-thaw deterioration of unsaturated rocks may still occur when a critical saturation is reached. This deterioration is caused by an accumulation of the long-term fatigue damage under freeze-thaw. Due to the importance of the clay-bearing rocks in geo-engineering practice, red sandstone is chosen to investigate the effect of water saturation on the physico-mechanical properties of clay-bearing rock by testing the uniaxial compressive strength (UCS) and P-wave velocity in laboratory. Besides, a fatigue damage model proposed by Liu et al. (Cold Reg Sci Technol 120:96–107, 2015) is improved and applied to evaluate the freeze-thaw damage degree and estimate the UCS after any freeze-thaw cycle. The research results suggest that freeze-thaw and water softening have an equally important influence on the clay-bearing red sandstone. In the absence of freeze-thaw, the UCS of red sandstone decreases with the increase of water saturation because of water weakening, including lubrication action, hydration of clay minerals, and dissolution of soluble minerals. However, more than 90% of UCS loss occurs at the range of the low degree of saturation below 60%. During freeze-thaw cycles, the critical saturation is about 60%, beyond which freeze-thaw damage grows quickly with increasing saturation and freeze-thaw cycles. Macro-cracks, initiating inside the clay minerals and propagating along the boundary of weather-resistant mineral grains, can be found on the surfaces of fully saturated specimens, while dried red sandstone keeps intact without obvious defects after 50 freeze-thaw cycles. Finally, the UCS of clay-bearing red sandstone with different water saturation is proved to be well predicted after any freeze-thaw cycle by the improved fatigue damage model.

Pore Structure Characteristics and Strength Variation of Red Sandstone under Freeze–Thaw Cycles

Effect of Different Moisture Content on Mechanical Parameters of Red Clay Under Freeze-Thaw Cycle

Experimental Investigation on Fracture Behavior and Mechanical Properties of Red Sandstone Subjected to Freeze–Thaw Cycles

Mechanical Characteristics of Red Sandstone Subjected to Freeze–Thaw Cycles and Increasing Amplitude Cyclic Load

Study on the mechanical properties of saturated red sandstone under freeze–thaw conditions

Effect of freeze–thaw cycle on physical and mechanical properties and damage characteristics of sandstone

Damage characteristics of sandstone pore structure under freeze-thaw cycles

Pore structure expansion and evolution in sandstone with prefabricated crack under freeze-thaw cycles based on CT scanning

Study on pore structure and the mechanical properties of sandstone-concrete binary under freeze-thaw environment

Study on Long-Term Dynamic Mechanical Properties and Degradation Law of Sandstone under Freeze-Thaw Cycle

Study on the Failure Process and Acoustic Emission Characteristics of Freeze–Thawed Sandstone under Cyclic Loading and Unloading

Effect of water saturation on uniaxial compressive strength and damage degree of clay-bearing sandstone under freeze-thaw

Study on the microscopic damage evolution and dynamic fracture properties of sandstone under freeze-thaw cycles

Strength degradation characteristics and damage constitutive model of sandstone under freeze–thaw cycles

NMR Pore Structure and Dynamic Characteristics of Sandstone Caused by Ambient Freeze-Thaw Action

Study on the pore structure characteristics and damage constitutive model of sandstone under freeze-thaw conditions

Coupled effects of chemical environments and freeze–thaw cycles on damage characteristics of red sandstone

Dynamic Mechanical Response and Dissipated Energy Analysis of Sandstone under Freeze-Thaw Cycles

Analysis of Microscopic Pore Characteristics and Macroscopic Energy Evolution of Rock Materials under Freeze-Thaw Cycle Conditions

Physical and mechanical characteristics deterioration and crack evolution of sandy mudstone in an open-pit mine under multiple freeze–thaw cycles

Dynamic tensile mechanical properties of water-saturated and frozen sandstone after freeze-thaw fatigue damage treatment