Abstract:Marine structures such as ports, bridges, pipelines, vessels, and platforms are an essential part of modern infrastructure, where the use of higher-strength steel provides savings in logistics and construction. However, the repair of higher-strength steels can be challenging, especially underwater. Wet shielded metal arc welding is the most widely used and least expensive method for underwater welding repairs, but is very susceptible to hydrogen-induced cracking. Thus, researchers and welding engineers aim to reduce the amount of hydrogen in the weld material. Recent success has been achieved through the use of austenitic welding consumables, such as austenitic stainless steel and nickel-based electrodes. The use of these consumables drastically reduces the amount of diffusible hydrogen in the weld metal. However, these austenitic materials usually have different corrosion potential as compared to the structural steel the weld beads are applied to. This creates the risk of severe galvanic corrosion. In the presented study, the corrosion behavior of welds created with austenitic stainless steel and nickel-based electrodes were studied. Samples were aged for 1.5 years in the Baltic Sea. Simultaneously, the effectiveness of corrosion protection systems such as coating and Impressed Current Cathodic Protection (ICCP) were evaluated. Localized corrosion occurred in the heat-affected zone when austenitic electrodes were used in the corrosive environment. The localized corrosion depth after 1.5 years in the Baltic Sea and in the salt spray layer was approximately 250 μm and 390 μm, respectively. The ICCP system and the use of a coating were effective in preventing localized corrosion. The low pitting corrosion density of 2.5 × 10 3 m −2 corresponds to grade A1 according to the standard and was found to be negligible as compared to the localized corrosion in the heat-affect zone.

Corrosion Mechanisms of Plasma Welded Nickel Aluminium Bronze Immersed in Seawater

Natural Seawater Impact on Crack Propagation and Fatigue Behavior of Welded Nickel Aluminum Bronze

Biofouling and corrosion rate of welded Nickel Aluminium Bronze in natural and simulated seawater

Corrosion Evolution of Nickel Aluminum Bronze in Clean and Sulfide-Polluted Solutions

Recent Advances Of Nickel-Aluminum Bronze (Nab)

Corrosion of Copper-Nickel Alloys in Seawater-Based Electrolytes

Cavitation Erosion Behavior of Nickel-Aluminum Bronze Weldment

Why does seawater corrosion significantly inhibit the cavitation erosion damage of nickel-aluminum bronze?

High Corrosion Resistance Nickel-Aluminum Bronze Prepared by Additive Manufacturing Followed by Laser Treatment

Perspectives on the unusual electrochemical corrosion of Nickel Aluminum Bronze (NAB) alloy fabricated through laser-powder bed fusion additive manufacturing

Correlation between microstructure and corrosion and cavitation erosion behaviors of nickel aluminum bronze

Evolution Of The Corrosion Product Film On Nickel-Aluminum Bronze And Its Corrosion Behavior In 3.5 Wt % Nacl Solution

Marine wear and tribocorrosion

Corrosion behavior of austenitic stainless steel and nickel-based welded joints in underwater wet welding

Effect of seawater salinity on the fretting corrosion behavior of nickel-aluminum bronze (NAB) alloy

Corrosion Behavior of 7A52 Aluminum Alloy Plasma Arc Welding Joint in Salt Water Spray

Cavitation erosion and corrosion behavior of copper–manganese–aluminum alloy weldment

A Review on Corrosion Behavior and Surface Modification Technology of Nickel Aluminum Bronze Alloys: Current Research and Prospects

Corrosion Behavior of Ni/NiCr/NiCrAlSi Composite Coating on Copper for Application as a Heat Exchanger in Sea Water

The Synergistic Effect of Cavitation Erosion and Corrosion of Nickel-Aluminum Copper Surface Layer on Nickel-Aluminum Bronze Alloy

Experimental investigation on wear resistance and corrosion behavior of nickel-aluminum bronze alloy fabricated by wire-arc additive manufacturing