Abstract:Mode-locked mid-infrared (mid-IR) fiber lasers are of increasing interest due to their many potential applications in spectroscopic sensors, infrared countermeasures, laser surgery, and high-efficiency pump sources for nonlinear wavelength convertors. Er3+-doped ZBLAN (ZrF4-BaF2-LaF3-AlF3-NaF) fiber lasers, which can emit mid-IR light at 2.65-2.9 mu m through the transition from the upper energy level I-4(11/2) to the lower laser level I-4(13/2), have attracted much attention because of their broad emission range, high optical efficiency, and the ready availability of diode pump lasers at the two absorption peaks of Er3+ ions (975 nm and 976 nm). In recent years, significant progress on high power Er3+-doped ZBLAN fiber lasers has been achieved and over 20 watt cw output at 2.8 mu m has been demonstrated; however, there has been little progress on ultrafast mid-IR ZBLAN fiber lasers to date. We report a passively mode-locked Er3+-doped ZBLAN fiber laser in which a Fe2+:ZnSe crystal was used as the intracavity saturable absorber. Fe2+:ZnSe is an ideal material for mid-IR laser pulse generation because of its large saturable absorption cross-section and small saturation energy along with the excellent opto-mechanical (damage threshold similar to 2 J/cm(2)) and physical characteristics of the crystalline ZnSe host. A 1.6 m double-clad 8 mol% Er3+-doped ZBLAN fiber was used in our experiment. The fiber core has a diameter of 15 mu m and a numerical aperture (NA) of 0.1. The inner circular cladding has a diameter of 125 mu m and an NA of 0.5. Both continuous-wave and Q-switched mode-locking pulses at 2.8 mu m were obtained. Continuous-wave mode locking operation with a pulse duration of 19 ps and an average power of 51 mW were achieved when a collimated beam traversed the Fe2+:ZnSe crystal. When the cavity was modified to provide a focused beam at the Fe2+:ZnSe crystal, Q-switched mode-locked operation with a pulse duration of 60 ps and an average power of 4.6 mW was achieved. More powerful and narrower pulses are expected if the dispersion of the cavity can be properly managed.

Highly efficient actively Q-switched Er^3+-doped ZBLAN fiber laser operating around 2.8 μm using a La_3Ga_5SiO_14 electro-optical modulator

165?MHz highly stable femtosecond Er:ZBLAN fiber laser operating at 2.8?μm

Experimental Investigation of High Power Pulsed 2.8 Μm Er3+-doped ZBLAN Fiber Lasers

Widely Wavelength Tunable Gain-Switched Er^3+-doped ZBLAN Fiber Laser Around 28 Μm

Widely wavelength tunable gain-switched Er<sup>3+</sup>-doped ZBLAN fiber laser around 2.8 μm.

Gain-Switched Er-Doped Fluoride Fiber Laser at ~3.75 μm

High Peak Power Actively Q-switched Mid-Infrared Fiber Lasers at 3 Μm

Q-Switched Mid-Infrared Er<sup>3+</sup>: ZBLAN Fiber Laser at 2.8 μm with a MXene-Based Saturable Absorber

Mid-infrared Pulsed Fiber Lasers Operating at 3μm Region

High-peak-power and wavelength tunable acousto-optic Q-switched Er:ZBLAN fiber laser

Widely tunable single-frequency Er-doped ZBLAN fiber laser with emission from 3.37 to 3.72 µm

Compact watt-level passively Q-switched ZrF4-BaF2-LaF3-AIF3-NaF fiber laser at 2.8 μm using Fe2+:ZnSe saturable absorber mirror

High power passively Q-switched Er3+-doped ZBLAN fiber laser at 2.8 µm based on a semiconductor saturable absorber mirror

State-switchable and Wavelength-Tunable Gain-Switched Mid-Infrared Fiber Laser in the Wavelength Region Around 2.94 Μm.

Pulsed Fluoride Fiber Lasers at 3 Μm [Invited]

Mid-infrared Q-switched Ho3+-doped Fluoride Fiber Laser

118 Nm-Wavelength-tunable Er3+-doped ZBLAN Passively Mode-Locked Fiber Laser

Modeling and Optimization of Actively Q-switched 2.8 Μm Er3+-doped ZBLAN Fiber Laser

Picosecond Passively Mode-Locked Mid-Infrared Fiber Laser

Q-Switched Mid-Infrared Er3+: Zblan Fiber Laser At 2.8 Mu M With A Mxene-Based Saturable Absorber

3.46 μm Q-switched Er3+:ZBLAN fiber laser based on a semiconductor saturable absorber mirror