Abstract:As a steel building may not fail in a fire scenario, the residual mechanical properties of steel after fire exposure are essential in evaluating the post-fire performance of the steel structure. However, the current experimental research regarding the post-fire mechanical properties neglects the stress in steel during the heating and cooling phases, which violates the fact that a steel structure still carries load during a fire hazard. In order to quantitatively assess the influence of stress level in steel structures on post-fire residual mechanical properties of high strength steels, a series of tensile tests was carried out on a typical high strength Q690 steel specimen exposed to elevated temperatures under three stress ratios, namely 0.30, 0.55 and 0.80. During the heating and cooling phases, constant stress was applied on the specimen to simulate the possible stress in steel structures in fire hazards. After cooling, tensile tests were carried out to attain the post-fire stress-strain curves of Q690 steel, and accordingly determine the residual yield strength, ultimate strength and elastic modulus of Q690 steel with different temperature exposures and stress levels. The test results show that the tension stress in steel during heating and cooling can improve the post-fire yield strength and ultimate strength of Q690 steel with the maximum 8% when the exposed temperature is lower than 700 °C, and the improvement increases as the stress level increases. However, the tension stress has adverse effect on the post-fire strengths of Q690 steel when the exposed temperature reaches 800 °C. If the exposed temperature is below 700 °C, it is safe to take the original strengths of Q690 steel to evaluate the post-fire performance of Q690 steel structures. However, the stress effect on the residual strengths should be considered if the exposed temperature reaches 800 °C to avoid unconservative evaluation. The tension stress in steel has no significant influence on residual elastic modulus of Q690 steel. By comparing the obtained test data with other post-fire tests on similar steels, it is found that the post-fire residual mechanical properties of steels are different even if those steels have the same nominal yield strength. The maximum 40% dispersion for residual yield strength and 50% dispersion for ultimate strength are found when the exposed temperature surpasses 600 °C due to rolling, quenching and tempering for high strength steels.

Tensile Tests for Material Characterisation of High- and Ultra-High-Strength Steels S690QL and S960QL under Natural Fire Conditions

Behavior of High Strength Structural Steel at Elevated Temperatures

Effects of sustained axial load and cooling phase on post-fire behaviour of concrete-filled steel tubular stub columns

Analysis of fracture behavior of high-strength steels in tension after fire exposure

Mechanical properties and design recommendations of very high strength steel S960 in fire

Experimental study on the post-fire mechanical behaviours of structural steels

Deterioration of Mechanical Properties of Novel Constructional Steel Material at Elevated Temperatures

Experimental study on post-fire mechanical properties and fracture behavior of Q690 steel

Experimental and numerical investigation on mechanical behavior of Q355 steel and connections in fire conditions

Post-fire mechanical properties and constitutive model of Q690 high-strength structural steel

Test on post-fire residual mechanical properties of high strength Q690 steel considering tensile stress in fire

Improved true stress-strain model of high-strength steels for fracture simulation in fire

Fracture behavior of Grade 10.9 high-strength bolts and T-stub connections in fire

High-Temperature Mechanical Properties of Artificially Simulated Corroded Q500MC Structural Steel

Post-fire Mechanical Properties of Q960 Cold-Formed Thick-Walled Ultra-High-Strength Steel

Experimental investigation of cold-formed steel material at elevated temperatures

Influence of test parameters on the high-temperature material properties of G550 CFS

Fracture behavior of high-strength steels at elevated temperatures

Strain-rate controlled Gleeble experiments to determine the stress-strain behavior of HSLA steel S960QL

High-cycle rotating-bending fatigue performance of S690QL welded joints

Material Behavior Description for a Large Range of Strain Rates from Low to High Temperatures: Application to High Strength Steel