Realizing High Comprehensive Energy Storage and Ultrahigh Hardness in Lead-Free Ceramics

Jie Xing,Yanli Huang,Qian Xu,Bo Wu,Qiming Zhang,Zhi Tan,Qiang Chen,Jiagang Wu,Jianguo Zhu
DOI: https://doi.org/10.1021/acsami.1c05153
2021-06-09
Abstract:Due to the presence of pores and low density, a high recoverable energy density (<i>W</i><sub>rec</sub>) value is usually obtained at the cost of energy storage efficiency (η) in lead-free potassium sodium niobate [(K, Na)NbO<sub>3</sub>, KNN] based ceramics, which also affects the hardness of ceramics, finally limiting the further development of practical applications. A high <i>W</i><sub>rec</sub> (∼3.60 J/cm<sup>3</sup> ) and a high η (∼74.2%) are obtained in 0.975K<sub>0.5</sub>Na<sub>0.5</sub>NbO<sub>3</sub>-0.025LaBiO<sub>3</sub> (0.975KNN-0.025LB) ceramics simultaneously under a high dielectric breakdown strength (DBS) of 340 kV/cm, together with a fast discharge rate (<i>t</i><sub>0.9</sub> ∼ 46 ns) and high power density (<i>P</i><sub>D</sub> ∼ 49.4 MW/cm<sup>3</sup>). Further analysis of the intrinsic electronic structure is carried out via the first-principles calculation based on the density functional theory (DFT). An ultrahigh hardness (<i>H</i>) of 6.63 GPa can be accordingly obtained. This work combines excellent energy storage properties and ultrahigh hardness, which provides significant guidelines for applications in pulsed-power systems.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c05153?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c05153</a>.Mechanical properties of KNN-xLB ceramics derived from Vickers indentation test (Table S1); SEM images of KNN-xBL ceramics (Figure S1); crystal structure parameters of KNN-xBL ceramics (Table S2); inverse dielectric permittivity as a function of temperature (Figure S2); vertical piezoelectric force microscopy (VPFM) images (Figure S3); vertical piezoresponse force microscopy (VPFM) amplitude (Figure S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05153/suppl_file/am1c05153_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
What problem does this paper attempt to address?